EFEITO DO TEOR DE PASTA E AGREGADOS FINOS NAS PROPRIEDADES DO CONCRETO DRENANTE

Pervious concretes were evaluated, prepared with blended portland cement, granitic coarse aggregates, variable contents of fine aggregate between 0 and 16 % and cement paste from 15 % to 25 % and incorporation of chemical admixtures. In the fresh state, the consistency was evaluated using the Abrams slump test and the Hand-Squeeze test. In the hardened state, were evaluated compressive strength at 7 and 28 days, apparent dry density, water absorption, void content, permeability and thickness of the cement paste surrounding the coarse aggregate. The size distribution of the internal pores was studied and a comparison is made between the porosity measured conventionally and by means of image analysis. Strength increased with fines content, with increasing paste content and with paste thickness, and simultaneously, void content and permeability decreased.Se evaluaron hormigones drenantes, elaborados con cemento portland compuesto, agregados gruesos graníticos, contenidos variables de agregado fino entre 0 y 16 % y de pasta desde 15 % a 25 % e incorporación de aditivos químicos. En estado fresco se evaluó la consistencia mediante el tronco de cono de Abrams y la prueba Hand-Squeeze. En estado endurecido, la resistencia a compresión a 7 y 28 días, la densidad seca aparente, la absorción, el contenido de vacíos, la permeabilidad y el espesor de la pasta circundante al agregado grueso. Se estudió la distribución de tamaño de los poros internos y se realizó una comparación entre la porosidad medida de forma convencional y por medio de análisis de imágenes. La resistencia aumentó con el contenido de finos, con el incremento del contenido de pasta y con el espesor de pasta y simultáneamente, se redujeron el contenido de vacíos y la permeabilidad.Foram avaliados concretos drenantes, elaborados com cimento portland composto, agregados graúdos graníticos, teores variáveis ​​de agregado miúdo entre 0 e 16% e pasta de 15% a 25% e incorporação de aditivos químicos.No estado fresco, a consistência foi avaliada por meio do tronco do cone de Abrams e do teste Hand-Squeeze. No estado endurecido, a resistência à compressão aos 7 e 28 dias, a densidade aparente a seco, a absorção, o índice de vazios, a permeabilidade e a espessura da pasta envolvendo o agregado graúdo.A distribuição de tamanho dos poros internos foi estudada e foi feita uma comparação entre a porosidade medida convencionalmente e por meio de análise de imagem.A resistência aumentou com o teor de finos, com o aumento do teor de pasta e com a espessura da pasta e, simultaneamente, o teor de vazios e a permeabilidade diminuíram