Tratamento de águas de refrigeração com peróxido de hidrogênio

Hydrogen peroxide and chlorine are compared as possible disinfectants for water-cooling circuits. To this purpose, samples taken from the cooling system of a steel making plant were treated (at 25ºC and pH values of 5.5 and 8.5) with varying amounts of the two oxidizing agents (0.0 mg/L, 2.0 mg/L and 6.0 mg/L). The results were evaluated through bacterial counting and measurement of corrosion rates upon AISI1020 carbon steel coupons. Bacterial removal and corrosion effects proved to be similar and satisfactory for both reagents

[pt] TRATAMENTO DE ÁGUAS DE RESFRIAMENTO COM PERÓXIDO DE HIDROGÊNIO

O tratamento de águas de resfriamento normalmente é feito com a adição de cloro, porém este produto apresenta algumas desvantagens em sua aplicação. Como alternativa ao cloro, algumas indústrias no Brasil e no exterior estão começando a utilizar outros biocidas, dentre estes o peróxido de hidrogênio, um poderoso oxidante que apresenta forte ação biocida. O objetivo deste trabalho foi comparar a eficiência do cloro e do peróxido de hidrogênio como biocidas em diferentes condições, através de testes em água da torre de resfriamento de uma indústria siderúrgica localizada no Rio de Janeiro. A contaminação microbiológica desta água foi medida sem a adição dos biocidas e com a adição de cloro e peróxido de hidrogênio, permitindo assim comparar o desempenho destas substâncias no combate aos grupos bacterianos presentes na amostra. Foi realizado também um estudo sobre o efeito corrosivo destas substâncias através de testes de corrosão em aço carbono 1020, que permitiram avaliar a taxa de corrosão por perda de massa provocada pela aplicação destes produtos na água. Os resultados mostraram que o peróxido de hidrogênio possui uma ação biocida satisfatória para aplicações em águas de resfriamento. Foi constatado que o efeito biocida do peróxido de hidrogênio é mais limitado do que o cloro e que sua eficiência depende do tempo de contato e pode ser afetada pela presença de impurezas dissolvidas na água. Os ensaios de corrosão revelaram que o peróxido de hidrogênio provoca um efeito corrosivo comparável ao do cloro no material testado.Cooling water treatment generally is made with the addition of chlorine, although it´s application has some disadvantages. There is an active development in Brazil and other countries to use alternative chemical disinfectants in place of chlorine, such as hydrogen peroxide, a powerful oxidant which is known for its high biocidal efficiency. The aim of this research is to study the effectiveness of hydrogen peroxide as a disinfectant compared to chlorine in different operational conditions. The experiments were carried out using an water sample from a cooling water system of a steelmaking plant in the city of Rio de Janeiro. The microbial contamination of this water sample was measured without adding any kind of disinfectant. After that, water sample was treated by adding hydrogen peroxide and chlorine, in order to compare and evaluate the efficiency of the two biocides to control bacterial growth in water. Besides microbiological tests, experiments were conducted to compare the degree of corrosion caused by the addition of hydrogen peroxide and chlorine in water. The experimental methodology employed 1020 carbon steel specimens and corrosion rates were measured by weight loss determination after the period of exposure. The results showed that the application of hydrogen peroxide leads to satisfactory bacterial control. However, compared to chlorine, hydrogen peroxide is a rather poor disinfectant. The efficiency of hydrogen peroxide depends on reaction time and it is affected by dissolved polluants in water. Evaluation of corrosion rates showed that hydrogen peroxide causes basically the same corrosion rates than chlorine