Susceptibility to Pitting Corrosion of Ti-CP2, Ti-6Al-2Sn-4Zr-2Mo, and Ti-6Al-4V Alloys for Aeronautical Applications

Titanium alloys are used in different industries like biomedical, aerospace, aeronautic, chemical, and naval. Those industries have high requirements with few damage tolerances. Therefore, they are necessary to use materials that present fatigue, mechanical, and corrosion resistance. Although Ti-alloys are material with high performance, they are exposed to corrosion in marine and industrial environments. This research shows the corrosion behavior of three titanium alloys, specifically Ti CP2, Ti-6Al-2Sn-4Zr-2Mo, and Ti-6Al-4V. Alloys were exposed on two electrolytes to a 3.5 wt % H2SO4 and NaCl solutions at room temperature using cyclic potentiodynamic polarization (CPP) and electrochemical noise (EN) according to ASTM G61 and ASTM G199 standards. CPP technique was employed to obtain electrochemical parameters as the passivation range (PR), corrosion type, passive layer persistence, corrosion potential (Ecorr), and corrosion rate. EN was analyzed by power spectral density (PSD) in voltage. Results obtained revealed pseudopassivation in CPP and PSD exposed on NaCl for Ti-6Al-2Sn-4Zr-2Mo, indicating instability and corrosion rate lower. However, Ti-6Al-4V presented the highest corrosion rate in both electrolytes. Ti-6Al-2Sn-4Zr-2Mo revealed pseudopassivation in CPP and PSD in NaCl, indicating a passive layer unstable. However, the corrosion rate was lower in both solutions

Corrosion Behavior of AA2055 Aluminum-Lithium Alloys Anodized in the Presence of Sulfuric Acid Solution

The aim of this work was to evaluate the corrosion behavior of the AA2055 Aluminum-lithium alloy anodized in a sulfuric acid (H2SO4) bath, varying the current density of 0.19 and 1 A·cm−2 and why the sealing solution was water (H2O) and sodium dichromate (Na2Cr2O7). Anodized samples were exposed to a 10 vol.% H2SO4 solution and the electrochemical technique used was electrochemical impedance spectroscopy. Scanning electron microscopy and X-ray photoelectron spectroscopy were employed to characterization of the anodizing layer, determinate morphology and thickness of coatings. The Na2Cr2O7 sealing solution tends to increase the charge transfer resistance and produces a more homogeneous and compact passive oxide layer, and imparts a corrosion inhibition protection to the AA2055. SEM observations indicated that the morphology and thickness of the anodic films formed on AA2055 aluminum-lithium alloy anodized have the best results for both current densities

Corrosion Behavior of Titanium Alloys (Ti CP2, Ti-6Al-2Sn-4Zr-2Mo, Ti-6Al-4V and Ti Beta-C) with Anodized and Exposed in NaCl and H₂SO₄ Solutions

Nowadays, different industries, such as the aerospace and biomedical industries, prefer using Ti alloys due to their excellent anti-corrosion properties and ability to generate a TiO2 oxide layer; this induces the use of anodization to increase the useful life of components. The aim of this work is to characterize the electrochemical effect of anodizing treatment on titanium alloys (Ti CP2, Ti-6Al-2Sn-4Zr-2Mo, Ti-6Al-4V, and Ti Beta-C) in NaOH and KOH at 1 M, applying a current density of 0.0025 A/cm2. The electrochemical techniques employed were electrochemical noise (EN) and electrochemical impedance spectroscopy (EIS), supported by ASTM G199 and ASTM G106 in electrolytes of NaCl and H2SO4 at 3.5 wt. % as a simulation of marine and industrial atmospheres. Also, the anodized transversal section and surface morphology were characterized by a scanning electron microscope (SEM). The results of both electrochemical techniques indicated that Ti-6Al-2Sn-4Zr-2Mo anodized in NaOH presented the best properties against corrosion, and the thickness of the oxide was the biggest