NASA welding assessment program

A long duration test has been conducted for comparing various methods of attaching electrical interconnects to solar cells for near Earth orbit spacecraft. Representative solar array modules have been thermally cycled for 36,000 cycles between -80 and +80 C on this JPL and NASA Lewis Research Center sponsored work. This test simulates the environmental stress of more than 6 years on a near Earth spacecraft as it cycles in and out of the Earth's shadow. Evaluations of the integrity of these modules were made by visual and by electrical examinations before starting the cycling and then at periodic intervals during the cycling tests. Modules included examples of parallel gap and of ultrasonic welding, as well as soldering. The materials and fabrication processes are state of the art, suitable for forming large solar arrays of spacecraft quality. The modules survived his extensive cycling without detectable degradation in their ability to generate power under sunlight illumination

NASA welding assessment program

A long duration test was conducted for comparing various methods of attaching electrical interconnects to solar cells for near Earth orbit spacecraft. Representative solar array modules were thermally cycled for 36,000 cycles between -80 and +80 C. The environmental stress of more than 6 years on a near Earth spacecraft as it cycles in and out of the earth's shadow was simulated. Evaluations of the integrity of these modules were made by visual and by electrical examinations before starting the cycling and then at periodic intervals during the cycling tests. Modules included examples of parallel gap and of ultrasonic welding, as well as soldering. The materials and fabrication processes are state of the art, suitable for forming large solar arrays of spacecraft quality. The modules survived this extensive cycling without detectable degradation in their ability to generate power under sunlight illumination

Ultrasonic seam welding on thin silicon solar cells

The ultrathin silicon solar cell has progressed to where it is a serious candidate for future light weight or radiation tolerant spacecraft. The ultrasonic method of producing welds was found to be satisfactory. These ultrathin cells could be handled without breakage in a semiautomated welding machine. This is a prototype of a machine capable of production rates sufficiently large to support spacecraft array assembly needs. For comparative purposes, this project also welded a variety of cells with thicknesses up to 0.23 mm as well as the 0.07 mm ultrathin cells. There was no electrical degradation in any cells. The mechanical pull strength of welds on the thick cells was excellent when using a large welding force. The mechanical strength of welds on thin cells was less since only a small welding force could be used without cracking these cells. Even so, the strength of welds on thin cells appears adequate for array application. The ability of such welds to survive multiyear, near Earth orbit thermal cycles needs to be demonstrated

Galileo Probe Battery System

The conclusions of the Galileo probe battery system are: the battery performance met mission requirements with margin; extensive ground-based and flight tests of batteries prior to probe separation from orbiter provided good prediction of actual entry performance at Jupiter; and the Li-SO2 battery was an important choice for the probe's main power