5 research outputs found
Surface modification of nanocrystalline LiMn2O4 using graphene oxide flakes
In this work, a facile, wet chemical synthesis was utilized to achieve a series of lithium manganese oxide (LiMn2O4, (LMO) with 1-5%wt. graphene oxide (GO) composites. The average crystallite sizes estimated by the Rietveld method of LMO/GO nanocomposites were in the range of 18-27 nm. The electrochemical performance was studied using CR2013 coin-type cell batteries prepared from pristine LMO material and LMO modified with 5%wt. GO. Synthesized materials were tested as positive electrodes for Li-ion batteries in the voltage range between 3.0 and 4.3 V at room temperature. The specific discharge capacity after 100 cycles for LMO and LMO/5%wt. GO were 84 and 83 mAh g(-1), respectively. The LMO material modified with 5%wt. of graphene oxide flakes retained more than 91% of its initial specific capacity, as compared with the 86% of pristine LMO material.Web of Science1415art. no. 413
Surface Oxidation of Nano-Silicon as a Method for Cycle Life Enhancement of Li-ion Active Materials
Among the many studied Li-ion active materials, silicon presents the highest specific capacity, however it suffers from a great volume change during lithiation. In this work, we present two methods for the chemical modification of silicon nanoparticles. Both methods change the materials’ electrochemical characteristics. The combined XPS and SEM results show that the properties of the generated silicon oxide layer depend on the modification procedure employed. Electrochemical characterization reveals that the formed oxide layers show different susceptibility to electro-reduction during the first lithiation. The single step oxidation procedure resulted in a thin and very stable oxide that acts as an artificial SEI layer during electrode operation. The removal of the native oxide prior to further reactions resulted in a very thick oxide layer formation. The created oxide layers (both thin and thick) greatly suppress the effect of silicon volume changes, which significantly reduces electrode degradation during cycling. Both modification techniques are relatively straightforward and scalable to an industrial level. The proposed modified materials reveal great applicability prospects in next generation Li-ion batteries due to their high specific capacity and remarkable cycling stability
Electrochemical Properties of Pristine and Vanadium Doped LiFePO<sub>4</sub> Nanocrystallized Glasses
In our recent papers, it was shown that the thermal nanocrystallization of glassy analogs of selected cathode materials led to a substantial increase in electrical conductivity. The advantage of this technique is the lack of carbon additive during synthesis. In this paper, the electrochemical performance of nanocrystalline LiFePO4 (LFP) and LiFe0.88V0.08PO4 (LFVP) cathode materials was studied and compared with commercially purchased high-performance LiFePO4 (C-LFP). The structure of the nanocrystalline materials was confirmed using X-ray diffractometry. The laboratory cells were tested at a wide variety of loads ranging from 0.1 to 3 C-rate. Their performance is discussed with reference to their microstructure and electrical conductivity. LFP exhibited a modest electrochemical performance, while the gravimetric capacity of LFVP reached ca. 100 mAh/g. This value is lower than the theoretical capacity, probably due to the residual glassy matrix in which the nanocrystallites are embedded, and thus does not play a significant role in the electrochemistry of the material. The relative capacity fade at high loads was, however, comparable to that of the commercially purchased high-performance LFP. Further optimization of the crystallites-to-matrix ratio could possibly result in further improvement of the electrochemical performance of nanocrystallized LFVP glasses
Electrochemical Properties of Pristine and Vanadium Doped LiFePO4 Nanocrystallized Glasses
In our recent papers, it was shown that the thermal nanocrystallization of glassy analogs of selected cathode materials led to a substantial increase in electrical conductivity. The advantage of this technique is the lack of carbon additive during synthesis. In this paper, the electrochemical performance of nanocrystalline LiFePO4 (LFP) and LiFe0.88V0.08PO4 (LFVP) cathode materials was studied and compared with commercially purchased high-performance LiFePO4 (C-LFP). The structure of the nanocrystalline materials was confirmed using X-ray diffractometry. The laboratory cells were tested at a wide variety of loads ranging from 0.1 to 3 C-rate. Their performance is discussed with reference to their microstructure and electrical conductivity. LFP exhibited a modest electrochemical performance, while the gravimetric capacity of LFVP reached ca. 100 mAh/g. This value is lower than the theoretical capacity, probably due to the residual glassy matrix in which the nanocrystallites are embedded, and thus does not play a significant role in the electrochemistry of the material. The relative capacity fade at high loads was, however, comparable to that of the commercially purchased high-performance LFP. Further optimization of the crystallites-to-matrix ratio could possibly result in further improvement of the electrochemical performance of nanocrystallized LFVP glasses
Correlation between Lithium Titanium Oxide Powder Morphology and High Rate Performance in Lithium-Ion Batteries
This study determined the measurable factor responsible for the high rate performance of lithium titanium oxide (Li4Ti5O12, LTO) powders in lithium-ion batteries. The structural and morphological properties of various Li4Ti5O12 materials and their correlation with electrochemical performance were analysed. The results showed that there was a strong correlation between high capacity retention at 10 C and the specific surface area. Other electrochemical and structural factors, such as the crystal size and pore structure, were not correlated with 10 C performance. We found that an increase in the specific surface area of Li4Ti5O12 above c.a. 15 m2 g−1 neither improved the high rate capacity retention nor its specific discharge capacity at high current rates. We also showed that the sol–gel synthesized lithium titanium oxide powders could retain similar or higher discharge specific capacities than materials synthesized via more complex routes