Polymerization shrinkage stress of composites photoactivated by different light sources

The purpose of this study was to compare the polymerization shrinkage stress of composite resins (microfilled, microhybrid and hybrid) photoactivated by quartz-tungsten halogen light (QTH) and light-emitting diode (LED). Glass rods (5.0 mm x 5.0 cm) were fabricated and had one of the surfaces air-abraded with aluminum oxide and coated with a layer of an adhesive system, which was photoactivated with the QTH unit. The glass rods were vertically assembled, in pairs, to a universal testing machine and the composites were applied to the lower rod. The upper rod was placed closer, at 2 mm, and an extensometer was attached to the rods. The 20 composites were polymerized by either QTH (n=10) or LED (n=10) curing units. Polymerization was carried out using 2 devices positioned in opposite sides, which were simultaneously activated for 40 s. Shrinkage stress was analyzed twice: shortly after polymerization (t40s) and 10 min later (t10min). Data were analyzed statistically by 2-way ANOVA and Tukey's test (a=5%). The shrinkage stress for all composites was higher at t10min than at t40s, regardless of the activation source. Microfilled composite resins showed lower shrinkage stress values compared to the other composite resins. For the hybrid and microhybrid composite resins, the light source had no influence on the shrinkage stress, except for microfilled composite at t10min. It may be concluded that the composition of composite resins is the factor with the strongest influence on shrinkage stress.Este estudo comparou a contração de polimerização de resinas compostas fotoativadas por luz halógena (QTH) e diodo emissor de luz (LED). Foram confeccionados bastões de vidro (5,0 mm x 5,0 cm), e uma de suas extremidades sofreu jateamento com óxido de alumínio, sobre a qual foi aplicado um adesivo e fotoativado com luz halógena. Os bastões de vidro foram acoplados verticalmente, em pares, em uma máquina universal de ensaios (EMIC DL-2000) e as resinas compostas aplicadas no bastão inferior. A distância entre os bastões foi padronizada em 2 mm e um extensômetro foi acoplado a eles. As resinas foram fotoativadas (n=20), sendo 10 por QTH e 10 por LED utilizando dois aparelhos posicionados em lados opostos, acionados simultaneamente por 40 s. A tensão de contração foi analisada em dois momentos: logo após a polimerização (t40s) e 10 min após (t10min). A tensão de contração apresentada por todas as resinas foi maior em t10min do que em t40s, independente da fonte ativadora. A resina de micropartículas apresentou menores valores de tensão de contração com valores estatisticamente significantes em relação às demais resinas. Para as resinas híbrida e microhíbrida não houve influência da unidade ativadora sobre a tensão de contração, com exceção para a resina de micropartículas em t10min. Concluiu-se que a composição da resina composta foi o fator que mais interferiu na tensão de contração da resina composta

Color stability of modern composites subjected to different periods of accelerated artificial aging

The aim of this study was to evaluate the color stability of composites subjected to different periods of accelerated artificial aging (AAA). A polytetrafluorethylene matrix (10 x 2 mm) was used to fabricate 24 test specimens of three different composites (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 and Z250 (3M ESPE), shade A3. After light activation for 20 s (FlashLite 1401), polishing and initial color readout (Spectrophotometer PCB 687; BYK Gardner), the test specimens were subjected to AAA (C-UV; Comexim), in 8-h cycles: 4 h exposure to UV-B rays at 50°C and 4 h condensation at 50°C. At the end of each cycle, color readouts were taken and the test ended when the mean value of ΔE attained a level ≥3.30. Tetric Ceram presented alteration in ΔE equal to 3.33 in the first aging cycle. For Filtek P90 and Z250, two (ΔE=3.60) and four (ΔE=3.42) AAA cycles were necessary. After each cycle, there was a reduction of luminosity in all the samples (ΔL). It was concluded that a short period of AAA was sufficient to promote clinically unacceptable color alteration in composites, and that this alteration was material-dependent

Shear bond strength of orthodontic brackets after accelerated artificial aging

O propósito deste estudo foi comparar a resistência ao cisalhamento (RC) e o índice de remanescente adesivo (IRA) após Envelhecimento Artificial Acelerado (EAA) de bráquetes ortodônticos metálicos fixados com compósitos autopolimerizável (Concise Ortodôntico - CS, 3M Unitek) e fotoativado (Transbond Plus Color Change - TPCC, 3M Unitek) com diferentes tratamentos de superfície do esmalte. Foram selecionados 60 pré-molares humanos recém extraídos, que tiveram suas raízes embutidas em resina acrílica ativada quimicamente de forma que a face vestibular ficasse perpendicular ao plano horizontal. Estas foram limpas com pedra pomes e água por 10 segundos, lavadas e secas. Os dentes foram separados aleatoriamente em 5 grupos (n=12), segundo o tipo de tratamento de superfície do esmalte, e do compósito utilizado para fixação dos bráquetes: Grupo I - ácido fosfórico a 37% (Dental Gel, Dentsply) e CS; Grupo II - ácido fosfórico a 37% + Primer e CS; Grupo III - ácido fosfórico a 37% e TPCC; Grupo IV - ácido fosfórico a 37% + XT Primer (3M Unitek) e TPCC; e Grupo V Transbond Plus Self Etching Primer - SEP (3M Unitek) e TPCC. Após 24h da colagem dos bráquetes, metade das amostras de cada grupo (n=6) foi submetida ao EAA por 960 horas. Todas as amostras foram submetidas ao ensaio de resistência ao cisalhamento com cinzel em máquina universal de ensaios (DL 200, EMIC) na velocidade de 0,5 mm/min. Após a descolagem dos bráquetes, causada pelo teste de resistência ao cisalhamento, o IRA foi avaliado em lupa (10X) e quantificado a partir de escore (0-3). Os dados foram analisados estatisticamente (2-way ANOVA, Bonferroni, p0,05). Quando comparados os sistemas adesivos utilizados, verificou-se que o Grupo II sem EAA, apresentou a maior média de RC, resultado estatisticamente significante (p0.05). When comparing the adhesive systems used, it was verified that Group II without AAA showed the highest mean SBS, a statistically significant result (p<0.05) in comparison with Groups III and V, which showed the lowest mean SBS. As regards ARI, all the groups without AAA showed higher frequency of Index 3. With AAA, there was increased frequency of indexes 1 and 2. It was concluded that AAA did not influence SBS of brackets to the tooth, but diminished the area of adhesive remnant on the tooth