43 research outputs found
High-velocity-oxidation performance of metal-chromium-aluminum (MCrAl), cermet, and modified aluminide coatings on IN-100 and type VIA alloys at 1093 C
Cermet, MCrAl, and modified aluminide types of coatings applied to IN-100 and NASA-TRW-VIA alloy specimens were cyclically oxidation tested in a high velocity (Mach 1) gas flame at 1093 C. Several coating compositions of each type were evaluated for oxidation resistance. The modified aluminide coating, Pt-Al, applied to alloy 6A proved to be the best, providing oxidation protection to approximately 750 hours based on weight change measurements. The second best, a CoCrAlY coating applied to 6A, provided protection to 450 hours. The third best was a cermet + aluminide coating on 6A with a protection time to 385 hours
Vaporization of Tantalum Carbide-hafnium Carbide Solid Solutions at 2500 Deg to 3000 Deg k
Vaporization rates in vacuum of hot pressed tantalum carbide and hafnium carbide in temperature range of 2500 to 3000 deg
In-situ measurements of alloy oxidation/corrosion/erosion using a video camera and proximity sensor with microcomputer control
Two noncontacting and nondestructive, remotely controlled methods of measuring the progress of oxidation/corrosion/erosion of metal alloys, exposed to flame test conditions, are described. The external diameter of a sample under test in a flame was measured by a video camera width measurement system. An eddy current proximity probe system, for measurements outside of the flame, was also developed and tested. The two techniques were applied to the measurement of the oxidation of 304 stainless steel at 910 C using a Mach 0.3 flame. The eddy current probe system yielded a recession rate of 0.41 mils diameter loss per hour and the video system gave 0.27
Digital temperature and velocity control of mach 0.3 atmospheric pressure durability testing burner rigs in long time, unattended cyclic testing
Hardware and software were developed to implement the hybrid digital control of two Jet A-1 fueled Mach 0.3 burners from startup to completion of a preset number of hot corrosion flame durability cycle tests of materials at 1652 F. This was accomplished by use of a basic language programmable microcomputer and data aquisition and control unit connected together by the IEEE-488 Bus. The absolute specimen temperature was controlled to + or - 3 F by use of digital adjustment of the fuel flow using a P-I-D (Proportional-Integral-Derivative) control algorithm. The specimen temperature was within + or - 2 F of the set point more than 90 percent of the time. Pressure control was achieved by digital adjustment of the combustion air flow using a proportional control algorithm. The burner pressure was controlled at 1.0 + or - 0.02 psig. Logic schemes were incorporated into the system to protect the test specimen from abnormal test conditions in the event of a hardware of software malfunction
Application of induction coil measurements to the study of superalloy hot corrosion and oxidation
The assessment of the degree of hot corrosion attack on nickel based alloys is a difficult task, especially when the definition specifies that it must be in terms of metal consumed and even more difficult if the measurement must be nondestructive. The inductance of a solenoid coil responds to changes in volume of fill and composition of metal cores, therefore, it may be used for nondestructive measurement of hot corrosion. The hot corrosion of U700 was studied at 900 C in a Mach 0.3 flame doped with 0.85 wppm of sodium. The change of inductance was found to define the known corrosion behavior and to suggest its use as a tool with predictive capabilities. Sufficient sensitivity exists to detect oxidation of this alloy at 900 C
Cyclic oxidation of cobalt-chromium-aluminum-yttrium and aluminide coatings on IN-100 and VIA alloys in high velocity gases
Embedded-alumina-particle aluminide (EAPA) coated and CoCrAlY coated IN-100 and NASA-TRW-VIA specimens were cyclically oxidation tested in a high velocity (approximately Mach 1) gas flame at 1093 C (2000 F). The EAPA coatings on both alloys performed very similarly to commercial pack aluminide coatings with respect to weight change and thermal fatigue cracking. The CoCrAlY coating on IN-100 had weight changes similar to commercial pack aluminide coatings but no thermal fatigue cracks appeared at 300 hours. The CoCrAlY coating on VIA performed significantly better than the commercial aluminide coatings, providing oxidation protection (based on weight change) to 450 hours and thermal fatigue crack prevention to at least 600 hours
Effects of alloy composition on cyclic flame hot-corrosion attack of cast nickel-base superalloys at 900 deg C
The effects of Cr, Al, Ti, Mo, Ta, Nb, and W content on the hot corrosion of nickel base alloys were investigated. The alloys were tested in a Mach 0.3 flame with 0.5 ppmw sodium at a temperature of 900 C. One nondestructive and three destructive tests were conducted. The best corrosion resistance was achieved when the Cr content was 12 wt %. However, some lower-Cr-content alloys ( 10 wt%) exhibited reasonable resistance provided that the Al content alloys ( 10 wt %) exhibited reasonable resistance provided that the Al content was 2.5 wt % and the Ti content was Aa wt %. The effect of W, Ta, Mo, and Nb contents on the hot-corrosion resistance varied depending on the Al and Ti contents. Several commercial alloy compositions were also tested and the corrosion attack was measured. Predicted attack was calculated for these alloys from derived regression equations and was in reasonable agreement with that experimentally measured. The regression equations were derived from measurements made on alloys in a one-quarter replicate of a 2(7) statistical design alloy composition experiment. These regression equations represent a simple linear model and are only a very preliminary analysis of the data needed to provide insights into the experimental method
Silicon-slurry/aluminide coating
A low cost coating protects metallic base system substrates from high temperatures, high gas velocity ovidation, thermal fatigue and hot corrosion and is particularly useful fo protecting vanes and blades in aircraft and land based gas turbine engines. A lacquer slurry comprising cellulose nitrate containing high purity silicon powder is sprayed onto the superalloy substrates. The silicon layer is then aluminized to complete the coating. The Si-Al coating is less costly to produce than advanced aluminides and protects the substrates from oxidation and thermal fatigue for a much longer period of time than the conventional aluminide coatings. While more expensive Pt-Al coatings and physical vapor deposited MCrAlY coatings may last longer or provide equal protection on certain substrates, the Si-Al coating exceeded the performance of both types of coatings on certain superalloys in high gas velocity oxidation and thermal fatigue and increased the resistance of certain superalloys to hot corrosion
Method of protecting a surface with a silicon-slurry/aluminide coating
A low cost coating for protecting metallic base system substrates from high temperatures, high gas velocity oxidation, thermal fatigue and hot corrosion is described. The coating is particularly useful for protecting vanes and blades in aircraft and land based gas turbine engines. A lacquer slurry comprising cellulose nitrate containing high purity silicon powder is sprayed onto the superalloy substrates. The silicon layer is then aluminized to complete the coating. The Si-Al coating is less costly to produce than advanced aluminides and protects the substrate from oxidation and thermal fatigue for a much longer period of time than the conventional aluminide coatings. While more expensive Pt-Al coatings and physical vapor deposited MCrAlY coatings may last longer or provide equal protection on certain substrates, the Si-Al coating exceeded the performance of both types of coatings on certain superalloys in high gas velocity oxidation and thermal fatigue. Also, the Si-Al coating increased the resistance of certain superalloys to hot corrosion
An experimental, low-cost, silicon slurry/aluminide high-temperature coating for superalloys
A duplex silicon-slurry/aluminide coating has been developed and cyclically tested in Mach 1 combustion gases for oxidation and thermal fatigue resistance at 1093 C and in Mach 0.3 gases for hot-corrosion resistance at 900 C. The base-metal superalloys were VIA and B-1900. The coated B-1900 specimens performed much better in oxidation than similar specimens coated with aluminides and almost as well as the more-expensive Pt-Al and MCrAlY (where M is Ni and/or Co) coatings deposited by the physical vapor deposition process. The coating also provided good hot-corrosion protection. Metallographic, X-ray, and electron microprobe studies were made to characterize the coating, determine failure mechanisms, and study some of the changes due to exposure