Flexural strength and elastic modulus of ambient-cured blended low-calcium fly ash geopolymer concrete

Fly ash geopolymer is an emerging alternative binder with low environmental impact and potential to enhance sustainability of concrete construction. Most previous works examined the properties of fly ash-based geopolymer concrete (GPC) subjected to curing at elevated temperature. To extend the use of GPC in cast-in-situ applications, this paper investigated the properties of blended low-calcium fly ash geopolymer concrete cured in ambient condition. Geopolymer concretes were produced using low-calcium fly ash with a small percentage of additive such as ground granulated blast furnace slag (GGBFS), ordinary Portland cement (OPC) or hydrated lime to enhance early age properties. Samples were cured in room environment (18–23 °C and 70 ± 10% relative humidity) until tested. The results show that, density of hardened GPC mixtures is similar to that of normal-weight OPC concrete. Inclusion of additives enhanced the mechanical strengths significantly as compared to control concrete. For similar compressive strength, flexural strength of ambient cured GPC was higher than that of OPC concrete. Modulus of elasticity of ambient cured GPC tend to be lower than that of OPC concrete of similar grade. Prediction of elastic modulus by Standards and empirical equations for OPC concrete were found not conservative for GPC. Thus, an equation for conservative prediction of elastic modulus of GPC is proposed

The influence of rice husk ash addition on the properties of metakaolin-based geopolymers

This paper investigates the replacement of metakaolin (MK) with rice husk ash (RHA) in the production of alkali-activated binders or geopolymers. The influence of the RHA addition on compressive and flexural strength, as well as water absorption and apparent porosity were determined, in terms of the percentage of RHA in the mixture and molar ratios of the mixes. Fourier Transform Infrared (FTIR) spectroscopy and Energy Dispersive spectroscopy (EDS) were carried out to assess the changes in the microstructure of the geopolymer matrices with the RHA addition. Results have shown that RHA may be a supplementary precursor for geopolymers. The composition of the geopolymer matrices containing 0-40% RHA is very similar, which indicates that the additional Si provided by RHA is not incorporated to the geopolymer matrix. In addition, geopolymers with RHA content higher than 40% present a plastic behavior, characterized by extremely low strength and high deformation, which can be attributed to the formation of silica gel in formulations containing variable Si/Al ratio

Constraints on the χ_(c1) versus χ_(c2) polarizations in proton-proton collisions at √s = 8 TeV

The polarizations of promptly produced χ_(c1) and χ_(c2) mesons are studied using data collected by the CMS experiment at the LHC, in proton-proton collisions at √s=8  TeV. The χ_c states are reconstructed via their radiative decays χ_c → J/ψγ, with the photons being measured through conversions to e⁺e⁻, which allows the two states to be well resolved. The polarizations are measured in the helicity frame, through the analysis of the χ_(c2) to χ_(c1) yield ratio as a function of the polar or azimuthal angle of the positive muon emitted in the J/ψ → μ⁺μ⁻ decay, in three bins of J/ψ transverse momentum. While no differences are seen between the two states in terms of azimuthal decay angle distributions, they are observed to have significantly different polar anisotropies. The measurement favors a scenario where at least one of the two states is strongly polarized along the helicity quantization axis, in agreement with nonrelativistic quantum chromodynamics predictions. This is the first measurement of significantly polarized quarkonia produced at high transverse momentum