Low velocity impact modeling in composite laminates capturing permanent indentation

This paper deals with impact damage and permanent indentation modeling. A numerical model has been elaborated in order to simulate the different impact damage types developing during low velocity/low energy impact. The three current damage types: matrix cracking, fiber failure and delamination, are simulated. Inter-laminar damage, i.e. interface delamination, is conventionally simulated using interface elements based on fracture mechanics. Intra-laminar damage, i.e. matrix cracks, is simulated using interface elements based on failure criterion. Fiber failure is simulated using degradation in the volume elements. The originality of this model is to simulate permanent indentation after impact with a ‘‘plastic-like’’model introduced in the matrix cracking elements. This model type is based on experimental observations showing matrix cracking debris which block crack closure. Lastly, experimental validation is performed, which demonstrates the model’s satisfactory relevance in simulating impact damage. This acceptable match between experiment and modeling confirms the interest of the novel approach proposed in this paper to describe the physics behind permanent indentation

Modelling of impact damage and permanent indentation on laminate composite plate

This paper deals with impact damage and permanent indentation modelling. A model enabling the formation of damages developing during a low velocity / low energy impact test on laminate composite panels has been elaborated. The different impact damages developing during an impact test, i.e. matrix cracking, fibres failure and interfaces delamination, are simulated. The interlaminar damages, i.e. interfaces delamination, are classically simulated thanks to interface finite elements based on the fracture mechanics. The particularity of this model is to account for the intralaminar damages, i.e. matrix cracks, thanks to interface finite elements which respect their discontinue character. These interface elements allow equally to simulate the permanent indentation during the impact unloading. This impact mark modelling is very original in the literature, and should allow to entirely design a composite structure thanks to impact damage tolerance

Digital communications applied to underwater acoustics

Peer Reviewe