11 research outputs found
On Ti-18Si-6B and Ti-7.5Si-22.5B powder alloys prepared by high-energy ball milling and sintering
Recommended from our members
Oxidation Behavior of Mo-Si-B Alloys in Wet Air
Multiphase composite alloys based on the Mo-Si-B system are candidate materials for ultra-high temperature applications. In non load-bearing uses such as thermal barrier coatings or heat exchangers in fossil fuel burners, these materials may be ideally suited. The present work investigated the effect of water vapor on the oxidation behavior of Mo-Si-B phase assemblages. Three alloys were studied: Alloy 1 = Mo{sub 5}Si{sub 3}B{sub x} (T1)- MoSi{sub 2}- MoB, Alloy 2 = T1- Mo{sub 5}SiB{sub 2} (T2)- Mo{sub 3}Si, and Alloy 3 = Mo- T2- Mo{sub 3}Si. Tests were conducted at 1000 and 1100C in controlled atmospheres of dry air and wet air nominally containing 18, 55, and 150 Torr H{sub 2}O. The initial mass loss of each alloy was approximately independent of the test temperature and moisture content of the atmosphere. The magnitude of these initial losses varied according to the Mo content of the alloys. All alloys formed a continuous, external silica scale that protected against further mass change after volatilization of the initially formed MoO{sub 3}. All alloys experienced a small steady state mass change, but the calculated rates cannot be quantitatively compared due to statistical uncertainty in the individual mass measurements. Of particular interest is that Alloy 3, which contains a significant volume fraction of Mo metal, formed a protective scale. All alloys formed varying amounts of subscale Mo and MoO{sub 2}. This implies that oxygen transport through the external silica scale has been significantly reduced. For all alloys, water vapor accelerated the growth of a multiphase interlayer at the silica scale/unoxidized alloy interface. This interlayer is likely composed of fine Mo and MoO{sub 2} that is dispersed within a thin silica matrix. Alloy 3 was particularly sensitive to water accelerated growth of this interlayer. At 1100 C, the scale thickness after 300 hours increased from about 20 mm in dry air to nearly 100 mm in wet air
Recommended from our members
Effects of Wet Air and Synthetic Combustion Gas Atmospheres on the Oxidation Behavior of Mo-Si-B Alloys
Continuing our work on understanding the oxidation behavior of multiphase composite alloys based on the Mo-Si-B system, we investigated three alloys in the Mo-Si-B system, designated as A1, A2, and A3. The nominal phase assemblages of these alloys are: A1 = Mo{sub 5}Si{sub 3}B{sub x} (T1)-MoSi{sub 2}-MoB, A2 = T1-Mo{sub 5}SiB{sub 2} (T2)-Mo{sub 3}Si, and A3 = Mo-T2-Mo{sub 3}Si. Our previous work showed that for exposures to 1100 C, all alloys formed a protective oxide scale in dry air. Exposures to wet air containing about 150 Torr water promoted the formation of a multiphase layer near the scale/alloy interface composed of Mo and MoO{sub 2}. Interrupted mass loss measurements indicated a near zero mass change. In the present study, isothermal mass measurements were conducted in order to quantitatively determine the oxidation rate constants at 1000 C in both dry and wet air. These measurements are critical for understanding the nature of scale development during the initial exposure, as well as the nature of scale stability during the long-term exposure. Isothermal measurements were also conducted at 1600 C in dry air to make an initial determination of alloy stability with respect to Vision 21 goals. We also conducted alloy oxidation testing in a synthetic oxidizing combustion atmosphere. Alloys were exposed up to 300 hours at 1100 C to a gas mixture having an approximate gas composition of N{sub 2} - 13 CO{sub 2} - 10 H{sub 2}O - 4 O{sub 2}. This gas composition simulates oxidizing flue gas, but does not contain a sulfidizing agent that would also be present in flue gas. The oxidized samples were carefully analyzed by SEM/EDS. This analysis will be discussed to provide an understanding of the role of water vapor and the synthetic combustion atmosphere on the oxidative stability of Mo-Si-B alloys