    Effect of simplifications of bone and components inclination on the elastohydrodynamic lubrication modeling of metal-on-metal hip resurfacing prosthesis

    No full text
    It is important to study the lubrication mechanism of metal-on-metal hip resurfacing prosthesis in order to understand its overall tribological performance, thereby minimize the wear particles. Previous elastohydrodynamic lubrication studies of metal-on-metal hip resurfacing prosthesis neglected the effects of the orientations of the cup and head. Simplified pelvic and femoral bone models were also adopted for the previous studies. These simplifications may lead to unrealistic predictions. For the first time, an elastohydrodynamic lubrication model was developed and solved for a full metal-onmetal hip resurfacing arthroplasty. The effects of the orientations of components and the realistic bones on the lubrication performance of metal-on-metal hip resurfacing prosthesis were investigated by comparing the full model with simplified models. It was found that the orientation of the head played a very important role in the prediction of pressure distributions and film profiles of the metal-on-metal hip resurfacing prosthesis. The inclination of the hemispherical cup up to 45 had no appreciable effect on the lubrication performance of the metal-on-metal hip resurfacing prosthesis. Moreover, the combined effect of material properties and structures of bones was negligible. Future studies should focus on higher inclination angles, smaller coverage angle and microseparation related to the occurrences of edge loading. © IMechE 2012

    The role of vibration and drainage in femoral impaction bone grafting.

    No full text
    Vibration is commonly used in civil engineering applications to efficiently compact aggregates. This study examined the effect of vibration and drainage on bone graft compaction and cement penetration in an in vitro femoral impaction bone grafting model with the use of 3-dimensional micro-computed tomographic imaging. Three regions were analyzed. In the middle and proximal femoral regions, there was a significant increase in the proportion of bone grafts with a reciprocal reduction in water and air in the vibration-assisted group (P < .01) as compared with the control group, suggesting tighter graft compaction. Cement volume was also significantly reduced in the middle region in the vibration-assisted group. No difference was observed in the distal region. This study demonstrates the value of vibration and drainage in bone graft compaction, with implications therein for clinical application and outcome

    Vibration-assisted bone-graft compaction in impaction bone grafting of the femur

    No full text
    The complications of impaction bone grafting in revision hip replacement includes fracture of he femur and subsidence of the prosthesis. In this in vitro study we aimed to investigate whether the use of vibration, combined with a perforated tamp during the compaction of morsellised allograft would reduce peak loads and hoop strains in the femur as a surrogate marker of the risk of fracture and whether it would also improve graft compaction and prosthetic stability. We found that the peak loads and hoop strains transmitted to the femoral cortex during graft compaction and subsidence of the stem in subsequent mechanical testing were reduced. This innovative technique has the potential to reduce the risk of intra-operative fracture and to improve graft compaction and therefore prosthetic stability. © 2007 British Editorial Society of Bone and Joint Surgery

    Fretting corrosion of CoCr alloy: Effect of load and displacement on the degradation mechanisms

    No full text
    Fretting corrosion of medical devices is of growing concern, yet, the interactions between tribological and electrochemical parameters are not fully understood. Fretting corrosion of CoCr alloy was simulated, and the components of damage were monitored as a function of displacement and contact pressure. Free corrosion potential (Ecorr), intermittent linear polarisation resistance and cathodic potentiostatic methods were used to characterise the system. Interferometry was used to estimate material loss post rubbing. The fretting regime influenced the total material lost and the dominant degradation mechanism. At high contact pressures and low displacements, pure corrosion was dominant with wear and its synergies becoming more important as the contact pressure and displacement decreased and increased, respectively. In some cases, an antagonistic effect from the corrosion-enhanced wear contributor was observed suggesting that film formation and removal may be present. The relationship between slip mechanism and the contributors to tribocorrosion degradation is presented