109 research outputs found

    Examination of weld defects by computed tomography

    Get PDF
    Defects in metal arc gas (MAG) welds made in S235JR low carbon steel of 6 mm thickness were examined. A sample containing lack of fusion (LOF) and pores was examined by computed tomography ā€“ CT. The computed tomography examination was performed in order to define LOF size and position as well as dimensions and distribution of accompanying pores in the weld metal

    Ispitivanje greŔaka zavara kompjutorskom tomografijom

    Get PDF
    Defects in metal arc gas (MAG) welds made in S235JR low carbon steel of 6 mm thickness were examined. A sample containing lack of fusion (LOF) and pores was examined by computed tomography ā€“ CT. The computed tomography examination was performed in order to define LOF size and position as well as dimensions and distribution of accompanying pores in the weld metal.Ispitivane su greÅ”ke u zavarenom spoju niskougljičnog čelika S235JR debljine 6 mm zavarenog MAG postupkom. Uzorak koji sadrži greÅ”ke naljepljivanja i pore je ispitivan kompjutorskom tomografijom - KT. Programskom analizom tomografa je određena veličina i pozicija greÅ”aka naljepljivanja kao i dimenzije i raspored pratećih pora u zavarenom spoju

    Ispitivanje greŔaka zavara kompjutorskom tomografijom

    Get PDF
    Defects in metal arc gas (MAG) welds made in S235JR low carbon steel of 6 mm thickness were examined. A sample containing lack of fusion (LOF) and pores was examined by computed tomography ā€“ CT. The computed tomography examination was performed in order to define LOF size and position as well as dimensions and distribution of accompanying pores in the weld metal.Ispitivane su greÅ”ke u zavarenom spoju niskougljičnog čelika S235JR debljine 6 mm zavarenog MAG postupkom. Uzorak koji sadrži greÅ”ke naljepljivanja i pore je ispitivan kompjutorskom tomografijom - KT. Programskom analizom tomografa je određena veličina i pozicija greÅ”aka naljepljivanja kao i dimenzije i raspored pratećih pora u zavarenom spoju

    Fracture of drilling head pipe connection due to quenching of heat affected zone (HAZ)

    Get PDF
    The drilling head pipe connection is made of quenched and tempered steel 34CrNiMo6. The steel characteristic is high hardenability. Due to unsuitable and untested welding technology the heat affected zone (HAZ) cooling rate after welding surpassed the upper critical cooling rate. During horizontal drilling of the rock, the resulting brittle martensite could not bear the dynamic loads which led to a brittle fracture of the pipe connection

    Chemical and microstructural diversity of steel grades

    Full text link

    Osvrti: Hrvatsko sudjelovanje na Međunarodnim olimpijadama iz kemije

    Get PDF

    Metallurgical reactions in the coalescence zone between a reinforcement and a base metal in reinforced brazed joints

    Get PDF
    Daily newspaper from Sapulpa, Oklahoma that includes local, state, and national news along with advertising

    Reaktionen mit N-(1-Benzotriazolylcarbonyl)-aminosauren. I. Synthese von Hydantoinen und Hydantoinsaure-amiden

    Get PDF
    Die N-(1-Benzotriazolylcarbonyl)-aminosiiuren (I) werden mit Thionylchlorid in die mit der BTCO-gruppe geschutzten Aminosiiure- chloride (II) uberftihrt. Die konnen dann mit verschiedenen Aminen, indirekt uber isolierbare N-(1-Benzotriazolylcarbonyl)- aminosiiureamiden (III), oder direkt in die entsprechend substituierten Hydantoinsiiure-amide (IV) umgesetzt werden. Die Verbindungen III unterliegen bei der Einwirkung von Alkalien einer Cyclisierungs-Eliminierungs-Reaktion und liefern die 3,5-substituierte Hydantoine (V)
    • ā€¦
    corecore