Fabrication of Tio2 and V2o5 Thin Films by Powder Coating Technique

Titanium dioxide (TiO2) and vanadium oxide (V2O5) in different mixing percentage (100, 50, 0)% from them powders as thin film on substrate of glass .the coating thickness was ( 0.37 ±0.03 μm ). Thin films were inspection by microphotographs with scanning electron microscopy (SEM) and x-ray diffraction (XRD). The results showed that thin films was prepared crystalline and also the compound (tio2, v2o5), and the structure was regular and smooth

EFFECT OF NANO-ALUMINA ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF RECYCLED CONCRETE

In this paper, the effect of using recycle mortar as fine aggregate replacement and nano Alumina (Al2O3) powder replaced of cement on the concrete microstructure and their effect on the mechanical properties is investigated. The nano powder was used as additive to replaced (0.5, and 2. 5 wt %) of cement with recycle fine aggregate(RFA) to replacement (10,and 50 wt%) of natural fine aggregate in concrete mixture. The compressive strength and microstructure analysis tests were carried out on the concrete samples. Microstructure analysis tests were conducted using X-Ray Diffraction(XRD), Scanning Electron Microscopy(SEM), and Atomic Force Microscopy(AFM). Results shows that the nano-oxide and recycle aggregate addition leads to different microstructure of concrete. The high specific surface area of nano-oxide causes reduce calcium hydroxide Ca(OH)2 (CH) crystallite in the cement hydration process and the pores structure of calcium silicate hydrated gel lead to products denser and compacted microstructure, also the roughness of concrete surface was reduces which caused enhancement in the compressive strength with the addition of nano- Al2O3

Root and canal morphology of third molar teeth

Restorative and prosthetic considerations usually necessitates endodontic treatment of third molars in order to retain them as a functional component of the dental arch. However, the anatomy of third molars has been described as unpredictable. To date, there has been little published work on root and canal morphology of third molars, with an adequate sample size. The aim of this study was to investigate root and canal morphology of third molars. Maxillary and mandibular third molars were gathered from dental surgeries within north Jordan. Following access cavity preparation, pulp tissue was removed and root canals stained. Teeth were subject to examination after rendering them clear by immersion in methyl salicylate, and the following features evaluated: (1) number of roots; (2) number and type of root canals; (3) number and position of lateral canals; and (4) presence of inter-canal communications. Out of the examined 592 maxillary third molars, 69.9% had three roots, 10.81% had one, 9.79% had two, 9.12% had four, and 0.34% had five roots. Most had three (52.36%) and four canals (28.2%) with less frequency of two (11.48%), one (5.91%) and five canals (2.03%). Of the 639 mandibular third molars, 89.76% had two roots, 7.35% had three, 2.5% had one, and 0.47% had four roots. Most had three (55.71%) and two canals (29.42%) with less frequency of four (13.61%), one (1.09%) and five canals (0.15%). The majority of maxillary third molars had 3 roots, while the majority of mandibular third molars had two. Overall, nearly half of the maxillary and mandibular third molars had three canals. New canal configurations, not previously described in the literature nor included in Vertucci's classifications, were identified in both maxillary and mandibular third molars. 2023, The Author(s).The authors wish to thank Jordan University of Science & Technology for supporting this project.Scopu

Fabrication Of TiO2 , V2O5 Thin Film (Super Hydrophobic Surface )By Powder Coating Technique

In this research, deposition of titanium oxide (TiO2) and vanadium oxide (V2O5) thin film in different mixing percentage (0, 25 ,50, 75 and100)% on the substrate of glass .The coating thickness was ( 50 nm ). In this research contact angle was measured and the effect of weather conditions. Results showed that the value of the contact angle of the prepared films reached its highest value at 50% (TiO2+V2O5) was 160º. The results showed that the optical transmittance of TiO2 and V2O5 thin film decrease with increasing the deposition angle and decrease with increasing V2O5 proportion

Studying the effect of annealing on some electrical and optical properties for thin CdS , CdS:In films

In the present work we prepared heterojunction not homogenous CdS/:In/Cu2S) by spray and displacement methods on glass substrate , CdS:In films prepared by different impurities constration. Cu2S prepared by chemical displacement method to improve the junction properties , structural and optical properties of the deposited films was achieved . The study shows that the film polycrystalline by XRD result for all film and the energy gap was direct to 2.38 eV with no effect on this value by impurities at this constration