Texture gradient in a copper tube at maximum and minimum wall thickness

Tube drawing is an inhomogeneous process with anisotropic flow. Quantitative texture analysis was used to get inside in eccentricity and ovality of a Cu tube drawn without a plug. To obtain the texture gradient over the wall thickness high resolution synchrotron radiation was used. One obtains on one hand different textures at the surfaces than in the central region and the other hand a variation of the texture gradient at the maximum wall thickness of the tube compared to the minimum wall thicknes

A critical evaluation of microstructure-texture-mechanical behavior heterogeneity in high pressure torsion processed CoCuFeMnNi high entropy alloy

The present study aims to understand the evolution of textural and microstructural heterogeneity and its effect on evolution of mechanical properties of an equiatomic FCC CoCuFeMnNi high entropy alloy (HEA) disc subjected to high pressure torsion (HPT). HPT was performed on disc specimen with a hydrostatic pressure of 5 GPa for 0.1, 0.5, 1 and 5 turns at room temperature where the hardness saturated at 1941 MPa at the periphery of the sample after five turns. Synchrotron diffraction texture analysis of five-turn HPT sample reveals characteristic shear texture with the dominance of A and A* components near central region of the disc and it shifts to C {001} component near the periphery of the disc. X-ray diffraction analysis shows decrease in crystalline size with simultaneous increase in dislocation density for five-turn HPT sample with increasing strain from centre to the periphery of the disc. Microstructural analysis using electron back scatter diffraction and transmission electron microscopy indicates extensive grain fragmentation (≈55 nm) at the periphery of five-turn sample. The evolution of hardness from centre to the periphery of the disc cannot be explained only on the basis of evolution of grain size and dislocation density. The increase in contribution from solid solution strengthening due to partial dissolution of copper rich nano-clusters is expected to be the underlying cause for increase in the hardness. Thus, evolution of gradient microstructure, texture, and chemistry opens up new vistas for designing functionally graded materials for engineering applications