Magnetic thickness measurement for various iron steels using magnetic sensor and effect of electromagnetic characteristics

The diagnosis and prevention of the deterioration of iron-steel infrastructure has become an important social issue in recent years. The thickness measurement technique (extremely low-frequency eddy current testing (ELECT)) using a magnetic sensor for detecting steel corrosion at extreme frequency ranges has been previously reported. Using the calibration curves based on the correlation between the phase of the detected magnetic signal and the plate thickness, the plate thickness reduction caused by corrosion can be estimated from the detected phase signal. Iron-steel materials have large changes in electromagnetic characteristics; therefore, the reference calibration data for each type of iron-steel are required for plate thickness estimation. In this study, the effect of electromagnetic characteristics on the magnetic thickness measurement was investigated to improve the thickness estimation. Four types of iron-steel plates (SS400, SM400A, SM490A, and SMA400AW) with thicknesses ranging from 1 mm to 18 mm were measured by ELECT, and the phase change at multiple frequencies of each plate were analyzed. The shift in the phase and linearity regions of the calibration curves for each type of steel plate was observed. To analyze this shift phenomenon, the electromagnetic characteristics (permeability μ and conductivity σ) of each type of steel were measured. Compared with the permeability μ and conductivity σ of each steel plate in the applied magnetic field strength range, the product (σμ) for various steel plates decreased in the following order: SM400 > SS400 >SMA400AW > SM490A. The product of μ and σ is related to the skin depth, indicating the electromagnetic wave attenuation and eddy current phase shift in the material. Therefore, each shift in the calibration curve of each type of iron steel is explained by the changes in the parameters σ and μ

Thickness Measurement at High Lift-Off for Underwater Corroded Iron-Steel Structures Using a Magnetic Sensor Probe

Infrastructure facilities that were built approximately half a century ago have rapidly aged. Steel sheet piles, the inspection object in this study, are severely corroded, resulting in cave-in damages at wharfs. To solve such a problem, non-destructive inspection techniques are required. We previously demonstrated plate thickness measurement using extremely low-frequency eddy current testing. However, when the steel sheet piles are located in water, shellfish adhere to their surface, causing a lift-off of several tens of millimeters. Therefore, this large lift-off hinders the thickness measurement owing to fluctuations of magnetic signals. In this study, sensor probes with different coil diameters were prototyped and the optimum size for measuring steel sheet piles at high lift-off was investigated. Using the probes, the magnetic field was applied with a lift-off range from 0 to 80 mm, and the intensity and phase of the detected magnetic field were analyzed. Subsequently, by increasing the probe diameter, a good sensitivity was obtained for the thickness estimation with a lift-off of up to 60 mm. Moreover, these probes were used to measure the thickness of actual steel sheet piles, and measurements were successfully obtained at a high lift-off