Rheological Properties of Polyvinylacetate: Part II

The dynamic viscoelastic properties of Polyvinylacetate with molecular weight 83000g/mol (PVA 83K) were determined by using a Rheometer operated in the dynamic mode and 8 mm parallel plate over a wide range of temperature as a function of frequency. The measurements were performed successively in the parallel plate geometry using 8 mm plate instead of 25 mm. The glass plateau regime is clearly observed because we could measure PVA 83K sample successively under its glass temperature. The rheological properties of polydisperse PVA 83K were completely studied and the experimental data were analyzed using the Winter model

Dynamic Mechanical Analysis for Waste Tires Reinforced Polystyrene: Shear Compliance

Abstract: Polystyrene/waste tires composites were prepared in this study by incorporating small particles of waste tires into polydisperse commercial polystyrene (PS) in a melt-mixing method. The dynamic mechanical properties of PS and PS/composite were studied using ARES-Rheometer under nitrogen atmosphere in parallel plate geometry with diameter 8 mm. The measurements were carried out over a wide range of temperatures ranged from 120°C to 220°C and frequencies from 100 to 0.1 radians per second. The shear compliance of PS composite were studied and compared with those of unfilled PS. The shear compliance were studied and evaluated. Where the values of J' at = 0.06 radians/s are 110-4 and 5.310-5 Pa-1 for PS and PS composite, respectively At = 0.1 radians/s the addition of the rubber alters the value of J'' from 1.610-4 to 8.410-5 Pa-1. That means the stability of PS is enhanced by the incorporation of the rubbe

Rheological Properties of Polyvinylacetate: Compliance and Relaxation Spectrum

Abstract: The dynamic viscoelastic properties of Polyvinylacetate with molecular weight 83000g/mol (PVA 83K ) were determined by using a Rheometer operated in the dynamic mode and 8 mm parallel plate over a wide range of temperature as a function of frequency. The measurements were performed successively in the parallel plate geometry using 8 mm plate instead of 25 mm. The glass plateau regime is clearly observed because we could measure PVA 83K sample successively under its glass temperature. The rheological properties of polydisperse PVA 83K were completely studied. The storage and loss compliance and the relaxation spectrum are evaluated

Rheological Characterization of Bitumen/Waste Polyethylene Composites: Part III

Waste polyethylene (PE) bags were reused in the modification of commercially available bitumen. The bitumen/PE blend was prepared by mixing homogenously commercial bitumen with waste PE in the molten state. The samples of bitumen blend and bitumen base were rheologically analyzied. The rheological properties such as complex modulus, shear compliance, torque and complex viscosity of bitumen and bitumen blend were studied using an ARES- Rheometer (Rheometric Scientific, Co.) in the dynamic mode, plate-plate geometry with diameter 8 mm. The measurements were performed over a wide range of temperatures ranged from-10°C to 60°C and frequencies from 100 to 0.1 radians per second. The results evidence that the complex modulus, shear compliance, torque and viscosity are improved by the incorporation of the waste PE into bitumen. The flow activation energy for neat bitumen and bitumen-9%PE are calculated from 0 by using the rheometric software

Dynamic and Complex Viscosity of Polystyrene/ Waste Tires Composites

Abstract: In this work, polystyrene/waste tires composites were prepared using the melt-mixing method. The viscoelastic properties of PS and PS/composite have been evaluated and compared. These properties were studied using ARES-Rheometer under nitrogen atmosphere in parallel plate geometry with diameter 8 mm. The measurements are carried out over a wide range of temperatures ranged from 120°C to 220°C and frequencies from 100 to 0.1 radians per second. The dynamic and complex viscosity of the PS composites were studied and compared with those of unfilled PS. The results showed that the frequency, is shifted from 0.46 to 0.072 radians/s and the value of dynamic viscosity increases from 5.0104 to 1.3105 Pa.s by the addition of the rubber for PS. Zero-shear viscosity, 0 was found to be increased from is 9.5104 for PS/waste tire composite to 4.5104 for PS. The flow activation energy is calculated from 0 by using the rheometric software to be 1.063 105 and 1.46 105 J/mol.K for Ps and PS composite, respectively

Complex Modulus of Waste Tires Reinforced Polystyrene

Abstract: In this work, polystyrene/waste tires composites were prepared by incorporating of waste tires into polydisperse commercial polystyrene in a melt-mixing method. The rheological characterization of PS and PS/composite have been studied and compared. These properties were studied using ARES-Rheometer under nitrogen atmosphere in parallel plate geometry with diameter 8 mm. The measurements are carried out over a wide range of temperatures ranged from 120°C to 220°C and frequencies from 100 to 0.1 radians per second. The complex modulus (G*) were evaluated and compared with those of unfilled PS. The dynamic mechanical properties and stability at elevated temperatures were found to increase with the addition of waste tires to PS as confirmed by the results. The results showed that the value of G* at = 1.0 radian/s is 1.8104 and 4.4104 Pa for PS and PS/waste tires, respectively. This difference rises at low frequencies-branch to be the value of G* at = 0.06 radian/s is 8.8102 and 7.8103 Pa for PS and PS/waste tires, respectively. Generally G* increases by the addition of rubber as filler for P

INTERNET OF THINGS SECURITY DOMAIN NAME SYSTEM POLICY AND ANALYTICS

Techniques are described herein to allow each Domain Name System (DNS) packet to be identified by enterprise and device at the DNS server. The DNS server may apply security rules per device and generate reports and charts on a per device level of granularity for analytics about the traffic behavior/trend for each enterprise