Flux flow noise in high Tc superconductors thin films

We have studied the fraction pinned of vortex in a type II superconductors. The sample used is the YBa2Cu3O7-d thin films. This fraction pinned is determined from the comparison of the experimental results and the theoretical results previously definite. In continuation one will study the variations of this fraction according to the temperature of the applied magnetic field and the electric current crossing the sample.We have studied the fraction pinned of vortex in a type II superconductors. The sample used is the YBa2Cu3O7-d thin films. This fraction pinned is determined from the comparison of the experimental results and the theoretical results previously definite. In continuation one will study the variations of this fraction according to the temperature of the applied magnetic field and the electric current crossing the sample

The vortex motion and the magnetization study in YBa2Cu3O7-d single crystal

We have investigated the vortex motion and the magnetization of high critical temperature superconductors YBa2Cu3O7-d Measurements were made using a vibrating sample magnetometer technique. Several magnetization hysteresis cycles have been obtained for different angles, θ, between the applied magnetic field, H, and the crystallographic c-axis. For T = 30 K we observed a central peak and for T = 80 K we observed a second peak or "fishtail".We have investigated the vortex motion and the magnetization of high critical temperature superconductors YBa2Cu3O7-d Measurements were made using a vibrating sample magnetometer technique. Several magnetization hysteresis cycles have been obtained for different angles, θ, between the applied magnetic field, H, and the crystallographic c-axis. For T = 30 K we observed a central peak and for T = 80 K we observed a second peak or "fishtail"

The critical current density and the vortex pinning in high quality YBa2Cu3O7-d thin films

We have measured the critical current density Jc of high quality c-axis oriented YBa2Cu3O7-d thin films. Measurements were performed for various magnetic field and temperature values, and as a function of the angle q between the c-axis and the applied magnetic field direction. A maximum of the critical current density was obtained when the flux lines are aligned along the CuO planes (q = 90°); another maximum in Jc was also observed when the magnetic field is adjusted parallel to the c-axis. We attribute these effects to different, intrinsic and extrinsic, pinning mechanisms of vortices in the sample.We have measured the critical current density Jc of high quality c-axis oriented YBa2Cu3O7-d thin films. Measurements were performed for various magnetic field and temperature values, and as a function of the angle q between the c-axis and the applied magnetic field direction. A maximum of the critical current density was obtained when the flux lines are aligned along the CuO planes (q = 90°); another maximum in Jc was also observed when the magnetic field is adjusted parallel to the c-axis. We attribute these effects to different, intrinsic and extrinsic, pinning mechanisms of vortices in the sample