ТЕХНОЛОГИЧЕСКИЕ АСПЕКТЫ ПРОДЛЕНИЯ РЕСУРСА НАПРАВЛЯЮЩИХ ЛОПАТОК ТУРБИНЫ С ИСПОЛЬЗОВАНИЕМ ДИФФУЗИОННОЙ ПАЙКИ НА ЭТАПЕ ВОССТАНОВИТЕЛЬНОГО РЕМОНТА ГПА

A thorough damageability analysis of nozzle segments made of cobalt alloy FSX-414 has been performed during TVD operation. It was shown that the most typical defect of the segments is thermal fatigue cracking which decreases the life cycle of the machine parts. The most critical requirements to the repair technology have been determined. It was shown that the optimal method to eliminate thermal fatigue cracks is their cutting and further vacuum high temperature soldering. In this research, for the machine parts repair, Ni-Cr-Fe-Si-B solder was used; this solder allows formation of a regularly structured joint having acceptable level of strength and material plasticity at elevated temperatures.Проведен анализ повреждаемости сегментов соплового аппарата ТВД из кобальтового сплава FSX-414 в условиях эксплуатации. Показано, что наиболее характерным дефектом на сегментах являются трещины термической усталости, снижающие работоспособ­ность деталей. Определены основные требования к технологии ремонта указанных сег­ментов. Показано, что наиболее оптимальным способом устранения термоусталостных трещин является их разделка и последующая пайка в вакууме высокотемпературным припоем. В работе для ремонта деталей использован припой системы Ni—Cr—Fe—Si—B, позволяющий сформировать паяный шов с регулярной структурой, обеспечивающий прием­лемый уровень прочности и пластичности материала при повышенных температурах.