2.5MeV的He~+离子辐照316L不锈钢中氦泡的形核与生长研究

利用透射电子显微镜分析了０３—０５Ｔｍ温区（Ｔｍ为材料溶点）３１６Ｌ奥氏体不锈钢经高剂量氦离子辐照后辐照损伤峰区氦泡的形成行为实验结果支持氦泡的双原子形核模型，并证实氦泡的形成主要受制于自间隙子／氦置换机制扩散材料中高密度位错的存在显著增强氦泡形核并抑制氦泡生长与前人低剂量辐照实验结果的比较表明０３—０５Ｔｍ温区氦泡形核机制不随辐照剂量或剂量率发生显著变化．Specimens of 316L stainless steel are irradiated with 2.5 MeV He + ions at temperatures of 400,500 and 550℃,respectively.For each implantation the dose and dose rate are separately 2.5×10 21 ion/m 2 and (3 2—3 8)×10 16 ion/m 2s -1 .Bubble structures are investigated with cross sectional transmission electron microscopy(XTEM).The measured apparent activation energies provide evidence that the formation of bubbles is controlled by He diffusion via the self interstitial/He ...国家自然科学基金,国家高技术研究发展计划资

金属材料中氦的扩散与氦泡的形核生长研究

简述了金属材料中氦聚集行为的研究概况 ,特别是本课题组近年来对奥氏体不锈钢中氦扩散及氦泡形核生长机制的研究结果 ,并提出了这个领域有待解决的问题

ESTABLISHMENT AND APPLICATION OF INDIRECT ELISA METHOD FOR MEASURING THYMOSINα1CON-TENT IN THE TRANSGENIC Synochococcus sp.PCC7942WITH THYMOSINα1GENE

利用胸腺素α1(Tα1)_小牛血清白蛋白融合蛋白免疫新西兰兔获得的抗体 ,建立了Tα1间接酶联免疫吸附测定法 (ELISA) ,以定量检测转Tα1基因聚球藻7942外源基因表达产物胸腺素α1 ,实验结果表明该方法灵敏度高、专一性强、重复性好 ,可用于转基因微藻Tα1表达量的定量检测 ,同时表明Tα1基因能在聚球藻7942中稳定表达。The indirect ELISA method for measuring thymosinα1content in the transgenic Synochococcus sp.PCC7942with thymosinα1gene has been established by using the anti_thymosinα1-BSA fusion protein serum prepared in rabbits.The experiment reveals that the method is sensitive,specific and reliable.It can be used to measure content of thymosinα1expressed in transgenic Synochococcus sp.PCC7942with thymosinα1gene.It also shows that thymosinα1gene can be expressed steadily in Synochococcus sp.PCC7942.国家863计划(819-Q01)资助项

高温下He~＋辐照316L不锈钢时氦泡的形态及氦的俘获

用ＴＥＭ观察６００℃下氦离子辐照３１６Ｌ不锈钢中氦泡的形态及分布，发现氦浓度比较低时，氦泡优先在位错线上形成；随着氦浓度的增大，氦泡在基体中均匀分布．在晶粒内及品界处，氦泡都呈多面体形状，观察的晶界处不存在氦泡的优先生长现象．根据定量测得的氦泡直径和数密度的值，按“流体模型”描述的状态方程，计算处于可见氦泡中的氦浓度的深度分布，发现处于可见氦泡中的氦浓度分布相对于注入的氦浓度（ＴＲＩＭ计算）分布向表面方向发生位移．注入的氦基本上都处于可见氦泡之中

Study on Schottky barrier of 4H-SiC at different anealing temperature

采用磁控溅射的方法在4H-SiC样品上分别沉积四种金属薄膜(Ag,Cu,Ni,Cr)形成Schottky 接触,研究了不同温度退火对Schottky势垒高度的影响。通过对样品的I-V测试结果的拟合,得到各金属/4H-SiC Schottky接触的势垒高度以及理想因子。在反向偏压100V下,样品的反向漏电流小于10-10A,说明样品的反向特性良好。样品经过不同温度的退火后,发现Cu、Ni与4H-SiC的势垒高度(SBH)随退火温度的升高而提高,超过某一温度,其整流特性变差; Ag、Cr的SBH在退火后降低。SBH与金属功函数呈线性关系(Cr金属除外),斜率为0.11。Schottky barriers were formed by sputtering the metals on the front side of 4H-SiC(Si face) by magnetron sputtering to study the rectifying characteristics of the contacts between the metals and 4H-SiC. The infections of the annealing under different temperature were also studied. Schottky barrier height (SBH) of metal/4H-SiC was evaluated from I-V measurements. Under a reverse voltage about 100 V, the reverse leaky current is below 0.1 nA. After annealed, the SBH of Cu/, Ni/4H-SiC was increased, but the SBH of Cr/, Ag/4H-SiC contact was decreased. The relationship between the work function of metals and the SBH was presented. The barrier height depends on the metal work function with slopes of 0.1 to 0.2 (except metal Cr).福建省厦门市科技项目(3502Z20031076

辐照316L不锈钢的相变研究

运用穆斯堡尔效应和X射线衍射方法对辐照前后的316L不锈钢样品中的穆斯堡尔参数和相变进行了研究。实验表明316L不锈钢经能量为54MeV的碳离子辐照后,在结构和微观参数上都发生了重大变化。同时也对样品中碳的分布和相变的类型进行了探讨

高能氩离子辐照SiO_2玻璃的正电子寿命谱学研究

用 1.15GeV的氩离子在室温下对二氧化硅玻璃样品进行了辐照 ,并通过正电子寿命测量技术研究了辐照后材料微观结构的变化。结果表明 ,在未辐照二氧化硅玻璃中有近 81%的正电子是以正电子素的形式湮灭的 ;根据o -Ps的撞击湮灭寿命确定出未辐照样品的自由体积分布在0 .0 2— 0 .13nm3的区域里 ,平均自由体积半径约为 2 .5nm。辐照后材料的自由体积分布函数变窄 ,峰位下移 ,显示样品经辐照后有密度增大的现象。随着剂量的增大 ,第二正电子寿命成分的强度逐渐增加 ,而相应于o -Ps的寿命成分的强度逐渐减小 ,这被认为是由于辐照产生的电离电子在自由体积中漫游 ,使正电子与这些漫游电子发生湮灭的几率增大 ,从而减小了正电子素的形成几率

黄河流域环境演变与水沙运行规律研究

该项目为国家自然科学基金重大项目1988.7—1992.12,由中科院地理所主持,我所为三个完成单位之一；参加单位有清华、北大、黄委会等15个单位，我所由唐克丽主持，承担该项目中四个二级课题之一，经费占总经费的35%，为项目的重点课题，下设五个专题。鉴定意见如下：该成果的特色以黄河全流域上、中、下游相结合；环境演变与水沙运行规律研究相结合的多学科渗透；立足当前生产中急需解决的理论问题，面向全局2000年的前景进行预测，从而对黄河流域的综合治理与开发及其对黄河下游河道的影响，入黄泥沙等关键性和基础性问题的研究，取得了突破性的进展；对长期来一些争议性较大的问题做出了较明确的回答。从宏观角度对全流域进行了高层次的综合分析，预估了2030或2050年流域环境、水沙和河道演变发展趋势，提出了流域综合治理开发的方向，具有重大的科学意义和重要的实用价值。研究成果总体达到国际先进水平。我所主持的课题完成评价为优秀（A级）。一级证书共五名，我所唐克丽获一级证书。由我所主持的二级课题共颁发二级证书58份，我所参加者共获14份二级证书