Plasmonic Gold Helices for the visible range fabricated by oxygen plasma purification of electron beam induced deposits

Electron beam induced deposition (EBID) currently provides the only direct writing technique for truly three-dimensional nanostructures with geometrical features below 50 nm. Unfortunately, the depositions from metal-organic precursors suffer from a substantial carbon content. This hinders many applications, especially in plasmonics where the metallic nature of the geometric surfaces is mandatory. To overcome this problem a post-deposition treatment with oxygen plasma at room temperature was investigated for the purification of gold containing EBID structures. Upon plasma treatment, the structures experience a shrinkage in diameter of about 18 nm but entirely keep their initial shape. The proposed purification step results in a core-shell structure with the core consisting of mainly unaffected EBID material and a gold shell of about 20 nm in thickness. These purified structures are plasmonically active in the visible wavelength range as shown by dark field optical microscopy on helical nanostructures. Most notably, electromagnetic modeling of the corresponding scattering spectra verified that the thickness and quality of the resulting gold shell ensures an optical response equal to that of pure gold nanostructures

Aligned metal oxide nanotube arrays: key-aspects of anodic TiO2 nanotube formation and properties

Over the past ten years, self-aligned TiO2 nanotubes have attracted tremendous scientific and technological interest due to their anticipated impact on energy conversion, environment remediation and biocompatibility. In the present manuscript, we review fundamental principles that govern the self-organized initiation of anodic TiO2 nanotubes. We start with the fundamental question: Why is self-organization taking place? We illustrate the inherent key mechanistic aspects that lead to tube growth in various different morphologies, such as rippled-walled tubes, smooth tubes, stacks and bamboo-type tubes, and importantly the formation of double-walled TiO2 nanotubes versus single-walled tubes, and the drastic difference in their physical and chemical properties. We show how both double- and single-walled tube layers can be detached from the metallic substrate and exploited for the preparation of robust self-standing membranes. Finally, we show how by selecting the right growth approach to TiO2 nanotubes specific functional features can be significantly improved, e.g., an enhanced electron mobility, intrinsic doping, or crystallization into pure anatase at extremely high temperatures can be achieved. This in turn can be exploited in constructing high performance devices based on anodic TiO2 in a wide range of applications.Comment: from Nanoscale Horiz., 2016, Advance Articl

Magnetic control of flexible thermoelectric devices based on macroscopic 3D interconnected nanowire networks

Spin-related effects in thermoelectricity can be used to design more efficient refrigerators and offer novel promising applications for the harvesting of thermal energy. The key challenge is to design structural and compositional magnetic material systems with sufficiently high efficiency and power output for transforming thermal energy into electric energy and vice versa. Here, the fabrication of large-area 3D interconnected Co/Cu nanowire networks is demonstrated, thereby enabling the controlled Peltier cooling of macroscopic electronic components with an external magnetic field. The flexible, macroscopic devices overcome inherent limitations of nanoscale magnetic structures due to insufficient power generation capability that limits the heat management applications. From properly designed experiments, large spin-dependent Seebeck and Peltier coefficients of $-9.4$ $\mu$V/K and $-2.8$ mV at room temperature, respectively. The resulting power factor of Co/Cu nanowire networks at room temperature ($\sim7.5$ mW/K$^2$m) is larger than those of state of the art thermoelectric materials, such as BiTe alloys and the magneto-power factor ratio reaches about 100\% over a wide temperature range. Validation of magnetic control of heat flow achieved by taking advantage of the spin-dependent thermoelectric properties of flexible macroscopic nanowire networks lay the groundwork to design shapeable thermoelectric coolers exploiting the spin degree of freedom.Comment: 11 pages, 7 figure

Liquid Phase Infiltration of Block Copolymers

Novel materials with defined composition and structures at the nanoscale are increasingly desired in several research fields spanning a wide range of applications. The development of new approaches of synthesis that provide such control is therefore required in order to relate the material properties to its functionalities. Self-assembling materials such as block copolymers (BCPs), in combination with liquid phase infiltration (LPI) processes, represent an ideal strategy for the synthesis of inorganic materials into even more complex and functional features. This review provides an overview of the mechanism involved in the LPI, outlining the role of the different polymer infiltration parameters on the resulting material properties. We report newly developed methodologies that extend the LPI to the realisation of multicomponent and 3D inorganic nanostructures. Finally, the recently reported implementation of LPI into different applications such as photonics, plasmonics and electronics are highlighted