Development of Chitosan/Gelatin/Keratin Composite Containing Hydrocortisone Sodium Succinate as a Buccal Mucoadhesive Patch to Treat Desquamative Gingivitis

The aim of this research was to develop chitosan/gelatin/keratin composite containing hydrocortisone sodium succinate as a buccal mucoadhesive patch to treat desquamative gingivitis, which was fabricated through an environmental friendly process. Mucoadhesive films increase the advantage of higher efficiency and drug localization in the affected region. In this research, mucoadhesive films, for the release of hydrocortisone sodium succinate, were prepared using different ratios of chitosan, gelatin and keratin. In the first step, chitosan and gelatin proportions were optimized after evaluating the mechanical properties, swelling capacity, water uptake, stability, and biodegradation of the films. Then, keratin was added at different percentages to the optimum composite of chitosan and gelatin together with the drug. The results of surface pH showed that none of the samples were harmful to the buccal cavity. FTIR analysis confirmed the influence of keratin on the structure of the composite. The presence of a higher amount of keratin in the composite films resulted in high mechanical, mucoadhesive properties and stability, low water uptake and biodegradation in phosphate buffer saline (pH = 7.4) containing 104 U/ml lysozyme. The release profile of the films ascertained that keratin is a rate controller in the release of the hydrocortisone sodium succinate. Finally, chitosan/gelatin/keratin composite containing hydrocortisone sodium succinate can be employed in dental applications

An investigation into the effect of thickness of titanium dioxide and gold-silver nanoparticle titanium dioxide composite thin-films on photocatalytic activity and photo-induced oxygen production in a sacrificial system

Thin films of titanium dioxide and titanium dioxide with incorporated gold and silver nanoparticles were deposited onto glass microscope slides, steel and titanium foil coupons by two sol–gel dip-coating methods. The film's photocatalytic activity and ability to evolve oxygen in a sacrificial solution were assessed. It was found that photocatalytic activity increased with film thickness (from 50 to 500 nm thick samples) for the photocatalytic degradation of methylene blue in solution and resazurin redox dye in an intelligent ink dye deposited on the surface. Contrastingly, an optimum film thickness of [similar]200 nm for both composite and pure films of titanium dioxide was found for water oxidation, using persulfate (S2O82−) as a sacrificial electron acceptor. The nanoparticle composite films showed significantly higher activity in oxygen evolution studies compared with plain TiO2 films

Electrochemiluminescence (ECL) sensing properties of water soluble core-shell CdSe/ZnS quantum dots/Nafion composite films

Water soluble positively charged 2-(dimethylamino) ethanethiol (DAET)-protected core-shell CdSe/ZnS quantum dots (QDs) were synthesized and incorporated within negatively charged Nafion polymer films. The water soluble QDs were characterized using UV-visible and fluorescence spectroscopies. Nafion/QDs composite films were deposited on glassy carbon electrodes and characterized using cyclic voltammetry. The electrochemiluminescence (ECL) using hydrogen peroxide as co-reactant was enhanced for Nafion/QDs composite films compared to films of the bare QDs. Significantly, no ECL was observed for Nafion/QDs composite films when peroxydisulfate was used as the co-reactant, suggesting that the permselective properties of the Nafion effectively exclude the co-reactant. The ECL quenching by glutathione depends linearly on its concentration when hydrogen peroxide is used as the co-reactant, opening up the possibility to use Nafion/QDs composite films for various electroanalytical applications

Reverse-osmosis membranes by plasma polymerization

Thin allyl amine polymer films were developed using plasma polymerization. Resulting dry composite membranes effectively reject sodium chloride during reverse osmosis. Films are 98% sodium chloride rejective, and 46% urea rejective

Composite THz materials using aligned metallic and semiconductor microwires, experiments and interpretation

We report fabrication method and THz characterization of composite films containing either aligned metallic (tin alloy) microwires or chalcogenide As2Se3 microwires. The microwire arrays are made by stack-and-draw fiber fabrication technique using multi-step co-drawing of low-melting-temperature metals or semiconductor glasses together with polymers. Fibers are then stacked together and pressed into composite films. Transmission through metamaterial films is studied in the whole THz range (0.1-20 THz) using a combination of FTIR and TDS. Metal containing metamaterials are found to have strong polarizing properties, while semiconductor containing materials are polarization independent and could have a designable high refractive index. Using the transfer matrix theory, we show how to retrieve the complex polarization dependent refractive index of the composite films. We then detail the selfconsistent algorithm for retrieving the optical properties of the metal alloy used in the fabrication of the metamaterial layers by using an effective medium approximation. Finally, we study challenges in fabrication of metamaterials with sub-micrometer metallic wires by repeated stack-and-draw process by comparing samples made using 2, 3 and 4 consecutive drawings. When using metallic alloys we observe phase separation effects and nano-grids formation on small metallic wires

Nanocrystalline TiO2 and halloysite clay mineral composite films prepared by sol-gel method:Synergistic effect and the case of silver modification to the photocatalytic degradation of basic blue- 41 azo dye in water

Tubular halloysite clay mineral and nanocrystalline TiO2 were incorporated in the preparation of nanocomposite films on glass substrates via sol-gel method at 450 °C. The synthesis involves a simple chemical method employing nonionic surfactant molecule as pore directing agent along with the acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material and lead to the formation of TiO2 nanoparticles homogeneously distributed on the surface of the halloysite. Nanocomposite films without cracks of active anatase crystal phase and small crystallite size on halloysite nanotubes are characterized by microscopy techniques and porosimetry methods in order to examine their structural properties. The composite halloysite-TiO2 films with variable quantities of halloysite were examined as photocatalysts to the discoloration of Basic Blue 41 azo dye in water. These nanocomposite films proved to be very promising photocatalysts and highly effective to dye's discoloration in spite of small amount of halloysite/TiO2 catalyst immobilized onto glass substrates. It also has been shown that the efficiency of the halloysite/TiO2 films could be further improved when silver particles were deposited on their surface after successful adsorption from an aqueous solution of a silver salt and UV reduction of the adsorbed ions

Self-cleaning properties of TiO2/palygorskite and TiO2/halloysite nanocomposite coatings

Tubular halloysite and microfibrous palygorskite clay mineral combined with nanocrystalline TiO 2 are involved in the preparation of nanocomposite films on glass substrates via sol-gel route at 450°C. The synthesis employing nonionic surfactant molecule as pore directing agent along with the acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material lead to the formation of TiO 2 nanoparticles homogeneously distributed on the palygorskite and halloysite surfaces. Nanocomposite films without cracks of active anatase crystal phase on palygorskite and halloysite surfaces are characterized by microscopy techniques, UV-Vis spectroscopy, and porosimetry methods in order to examine their structural properties. The composite palygorskite- TiO 2 and halloysite/ TiO 2 films with variable quantities of palygorskite and halloysite were tested as photocatalysts in the photo-oxidation of Basic Blue 41 azo dye in water. These nanocomposite films proved to be most promising photocatalysts and highly effective to dye’s decoloration in spite of small amount of palygorskite/ TiO 2 or halloysite/ TiO 2 catalyst immobilized onto glass substrates

Enhanced self-field critical current density of nano-composite YBa(2)Cu(3)O(7) thin films grown by pulsed-laser deposition

This is the author's accepted manuscript. The final published article is available from the link below. Copyright @ EPLA, 2008.Enhanced self-field critical current density Jc of novel, high-temperature superconducting thin films is reported. Layers are deposited on (001) MgO substrates by laser ablation of YBa2Cu3O7−δ(Y-123) ceramics containing Y2Ba4CuMOx (M-2411, M=Ag, Nb, Ru, Zr) nano-particles. The Jc of films depends on the secondary-phase content of the ceramic targets, which was varied between 0 and 15 mol%. Composite layers (2 mol% of Ag-2411 and Nb-2411) exhibit Jc values at 77 K of up to 5.1 MA/cm2, which is 3 to 4 times higher than those observed in films deposited from phase pure Y-123 ceramics. Nb-2411 grows epitaxially in the composite layers and the estimated crystallite size is ~10 nm.The Austrian Science Fund, the Austrian Federal Ministry of Economics and Labour, the European Science Foundation and the Higher Education Commission of Pakistan

FERROCENYL ALKYLAMMONIUM N-SUBSTITUTED POLYPYRROLE CONTAINING Pt AND Pd AND ITS APPLICATION ON ELECTROANALYSIS OF ARSENITE

Indexación: Web of Science; Scopus; Scielo.Arsenic occurs in a variety of forms and oxidation states and is a very toxic element. The main inorganic arsenic species present in natural waters are arsenate (oxidation state V) and arsenite ions (oxidation state III). Arsenite is more toxic and mobile than arsenate. Therefore, it is important the development of new materials for analysis and control of these toxic species. This research proves that polymer-metal composite electrode materials synthesized by incorporation of Pt-0 and Pd-0 nanoparticles into a poly(pyrrole-ferrocenyl alkylammonium) matrix present electrocatalytic properties towards the oxidation of arsenite to arsenate. The polymer films displayed a stable electrochemical response in aqueous solution. However, when the polymer film modified electrode were transferred to aqueous solution in presence of arsenite anions, the CV curves for polymer films were deeply modified by the decrease in the electroactivity of the film. It can be concluded that the cationic polymer films present a strong affinity toward arsenite anions. The composite films containing Pt-0 or Pd-0 showed catalytic activity towards oxidation of As(III) to As(V) due to the presence of metal catalyst particles into the polymer films.http://ref.scielo.org/dgdvx

Magnetoelectric Effects on Composite Nano Granular Fe/TiO2−δFe/TiO_{2-\delta} Films

Employing a new experimental technique to measure magnetoelectric response functions, we have measured the magnetoelectric effect in composite films of nano granular metallic iron in anatase titanium dioxide at temperatures below 50 K. A magnetoelectric resistance is defined as the ratio of a transverse voltage to bias current as a function of the magnetic field. In contrast to the anomalous Hall resistance measured above 50 K, the magnetoelectic resistance below 50 K is significantly larger and exhibits an even symmetry with respect to magnetic field reversal $H\to -H$. The measurement technique required attached electrodes in the plane of the film composite in order to measure voltage as a function of bias current and external magnetic field. To our knowledge, the composite films are unique in terms of showing magnetoelectric effects at low temperatures, $<$ 50 K, and anomalous Hall effects at high temperatures, $>$ 50 K.Comment: ReVTeX, 2 figures, 3 page