Hormigón celular tratado en autoclave reforzado por pasadores poliméricos

Abstract

Autoclaved Aerated Concrete (AAC) is a lightweight and sustainable building material known for its thermal insulation and acoustic properties. However, its relatively low mechanical strength limits its use in load-bearing applications. This paper introduces the concept of incorporating unsaturated polyester resin (UPR) pins into AAC blocks to improve compressive and flexural strength of the material. Pin diameters of 4, 6, 8 and 10 mm were studied, oriented at 90° and 45° in relation to the AAC main plane. The effects of the UPR/AAC interface were analyzed through microscopy. The results point to a substantial increase in mechanical strength of the reinforced AAC, wherein smaller pins with orientation of 45° and 90° presented the best behavior under flexural (up to 298%) and compressive loading (up to 183%), respectively.Hormigón celular tratado en autoclave (AAC) es un material de construcción ligero y sostenible conocido por sus propiedades de aislamiento térmico y acústico. Sin embargo, su resistencia mecánica relativamente baja limita su uso en aplicaciones de carga. Este estudio introduce el concepto de incorporar pasadores de resina de poliéster insaturado (UPR) en bloques de AAC para mejorar la resistencia a la compresión y flexión del material. Se estudiaron diámetros de pasadores de 4, 6, 8 y 10 mm, orientados a 90° y 45° en relación al plano principal del AAC. Los efectos de la interfaz UPR/AAC fueron analizados a través de microscopía. Los resultados indican un aumento sustancial en la resistencia mecánica del AAC reforzado, donde los pasadores más pequeños con orientación de 45° (hasta un 298%) y 90° (hasta un 183%) presentaron el mejor comportamiento sobre esfuerzos de flexión y compresión, respectivamente