CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Mechanically-competent and cytocompatible polycaprolactone-borophosphosilicate hybrid biomaterials
Authors
S. Jeffrey Dixon
Kibret Mequanint
Dibakar Mondal
Amin S. Rizkalla
Publication date
1 November 2017
Publisher
Scholarship@Western
Abstract
© 2017 Organic-inorganic class II hybrid materials have domain sizes at the molecular level and chemical bonding between the organic and inorganic phases. We have previously reported the synthesis of class II hybrid biomaterials from alkoxysilane-functionalized polycaprolactone (PCL) and borophosphosilicate (B2O3-P2O5-SiO2) glass (BPSG) through a non-aqueous sol-gel process. In the present study, the mechanical properties and degradability of these PCL/BPSG hybrid biomaterials were studied and compared to those of their conventional composite counterparts. The compressive strength, modulus and toughness of the hybrid biomaterials were significantly greater compared to the conventional composites, likely due to the covalent bonding between the organic and inorganic phases. A hybrid biomaterial (50 wt% PCL and 50 wt% BPSG) exhibited compressive strength, modulus and toughness values of 32.2 ± 3.5 MPa, 573 ± 85 MPa and 1.54 ± 0.03 MPa, respectively; whereas the values for composite of similar composition were 18.8 ± 1.6 MPa, 275 ± 28 MPa and 0.76 ± 0.03 MPa, respectively. Degradation in phosphate-buffered saline was slower for hybrid biomaterials compared to their composite counterparts. Thus, these hybrid materials possess superior mechanical properties and more controlled degradation characteristics compared to their corresponding conventional composites. To assess in vitro cytocompatibility, MC3T3-E1 pre-osteoblastic cells were seeded onto the surfaces of hybrid biomaterials and polycaprolactone (control). Compared to polycaprolactone, cells on the hybrid material displayed enhanced spreading, focal adhesion formation, and cell number, consistent with excellent cytocompatibility. Thus, based on their mechanical properties, degradability and cytocompatibility, these novel biomaterials have potential for use as scaffolds in bone tissue engineering and related applications
Similar works
Full text
Available Versions
Scholarship@Western
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:ir.lib.uwo.ca:boneandjoint...
Last time updated on 23/11/2020