CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Acoustic characterization of polyvinyl chloride and self-healing silicone as phantom materials
Authors
Dennis Ceh
Elvis C.S. Chen
Terry M. Peters
Publication date
1 January 2015
Publisher
Scholarship@Western
Abstract
© 2015 SPIE. Phantoms are physical constructs used in procedure planning, training, medical imaging research, and machine calibration. Depending on the application, the material a phantom is made out of is very important. With ultrasound imaging, phantom materials used need to have similar acoustic properties, specifically speed of sound and attenuation, as a specified tissue. Phantoms used with needle insertion require a material with a similar tensile strength as tissue and, if possible, the ability to self heal increasing its overall lifespan. Soft polyvinyl chloride (PVC) and silicone were tested as possible needle insertion phantom materials. Acoustic characteristics were determined using a time of flight technique, where a pulse was passed through a sample contained in a water bath. The speed of sound and attenuation were both determined manually and through spectral analysis. Soft PVC was determined to have a speed of sound of approximately 1395 m/s and attenuation of 0.441 dB/cm (at 1 MHz). For the silicone mixture, the respective speed of sound values was within a range of 964.7 m/s and 1250.0 m/s with an attenuation of 0.547 dB/cm (at 1 MHz)
Similar works
Full text
Available Versions
Scholarship@Western
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:ir.lib.uwo.ca:biophysicspu...
Last time updated on 23/11/2020