Multi-Scale Finite Element Based Time-Dependent Reliability Analysis for Laminated Fibre Reinforced Composites

The objective of this paper is to propose a time-dependent reliability analysis method to investigate the durabil- ity of fibre reinforced polymer composites. A stochastic multi-scale finite element method, which is based on computational homogenization and perturbation technique, is adopted to propagate uncertainties in both micro- and macro-scale parameters. The influence of water absorption and heat conduction and the induced degradation of mechanical properties, which is estimated through a hygro-thermo-mechanical model that is integrated into the stochastic multi-scale finite method, is then studied in the framework of time-variant reliability analysis. It is shown that the problem reduces to a sequence of time-independent problems that can be solved using the first-order reliability method. A numerical study is carried out to demonstrate the applicability of the proposed method, and the evolution in time of the probability of failure is computed

Ulster University's Research Portal

Proceedings of the 24th UK Conference of theAssociation for Computational Mechanics in Engineering31 March - 01 April 2016, Cardi  University, Cardi MULTI-SCALE FINITE ELEMENT BASED TIME-DEPENDENTRELIABILITY ANALYSIS FOR LAMINATED FIBRE REINFORCEDCOMPOSITES*Xiao-Yi Zhou1, Peter D. Gosling1, Zahur Ullah2, Chris J. Pearce2 and Lukasz Kaczmarczyk21School of Civil Engineering & Geosciences, Newcastle University, Claremont road, NE1 7RU2School of Engineering, University of Glasgow, Oakfield avenue, Glasgow, G12 8QQ*xiaoyi.zhou@newcastle.ac.ukABSTRACTThe objective of this paper is to propose a time-dependent reliability analysis method to investigate the durabil-ity of fibre reinforced polymer composites. A stochastic multi-scale finite element method, which is based oncomputational homogenization and perturbation technique, is adopted to propagate uncertainties in both micro-and macro-scale parameters. The influence of water absorption and heat conduction and the induced degradationof mechanical properties, which is estimated through a hygro-thermo-mechanical model that is integrated intothe stochastic multi-scale finite method, is then studied in the framework of time-variant reliability analysis. It isshown that the problem reduces to a sequence of time-independent problems that can be solved using the first-orderreliability method. A numerical study is carried out to demonstrate the applicability of the proposed method, andthe evolution in time of the probability of failure is computed.Key Words: Composite; hygro-thermal e ect; computational homogenization; durability; reliability1. IntroductionComposite materials may provide benifits in terms of reduction of construction time and carbon emissionfor civil engineering sector, given their success in other sectors. However, civil engineering structures andinfrastructures are expected to serve in natural environment for 50 years or more. Accurately quantifyinglong term durability behaviour is eagerly needed to fully exploit benefits that composite materials couldbring to construction sector. In an on-going UK EPSRC funded research project - Providing Confidencein Durable Composites (DURACOMP), pultruded glass fibre reinforced composites, which are typicalconstruction composite materials, have been tested to characterize their ageing behaviours in hot/wetcondition. The evolution in time of moisture uptake ratio and mechanical properties has been measuredand reported in [1, 2]. To numerical simulate these coupon testing based findings to large scale structures,a coupled hygro-thermo-mechanical model has developed [3] to investigate the long term durabilityof composites in a deterministic context. Arising from various sources such as manufacturing process,assembly and quality control limits, composite materials exhibit uncertainties in their material properties.Taking these uncertainties into account in designing composites, such as through the use of reliabilitybased structural design, is essential to ensure that the structures perform with su cient safety duringtheir service and fully realize the advantages o ered by composites. In the present study, this coupledhygro-thermo-mechanical is combined with a probabilistic homogenization approach developed in [4] topropagate micro-scale uncertainties to the macro-scale in the mechanical problem. This is subsequentlyintegrated with reliability analysis methods to evaluate the reliability of composite structures.2. Time-dependent structural reliability analysisFor a stochastic structure system, when stochastic processes or functions of time are explicitly presentin the limit state function (LSF), g(x), time-variant analysis is required to quantify the probability offailure of the structure. Accordingly, the n-dimensional vector x that collects all random parameters in361the system is split into x1 which is a vector of random variables and x2(t) which is a vector of randomprocesses. The probability of failure, pf , of the structure within a time interval [tb, te] is defined aspf (tb, te ) = Pr (9t 2 [tb, te], g(x1, x2(t))  0) (1)In this study, the time e ect is present in the problem due to the degradation of material properties, theLSF g thus depends on random variables and functions of time. The computation of pf as defined inEq.(1) reduces topf , i = Pr (g (x1, x2(t))  0) (2)which is called instantaneous probability. In a degradation problem, the LSF is monotonously decreasingin time whatever the realizations of the random variables. For each realization of the random vector, theminimum value of g (x1, x2(t)) over a time interval [tb, te] is attained for t = te . Thus, the time-variantproblem is reduced to a time-invariant analysis to calculate the special case of Eq. (2) at te . First-orderreliability method (FORM) is one of the widely used methods to numerically estimate reliability for timeindependent problem. Essentially, it requires to transform random variables x from general probabilityspace to standard normal space as u, which leads to G(u), and to linearly approximate the LSF throughthe first-order Taylor series expansion, which needs to calculate gradient of G. According to the chainrule of di erentiation, the gradient vector of G can be obtained fromrG = @G@y=@g@ s@ s@x@x@y, (3)where @x@y is Jacobian of the probability transformation,@g@s can be analytically obtained since the LSFg is function of components of s. Thus, the only unknown is @s@x that will be calculated from stochasticfinite element method.3. Stochastic multi-scale finite element analysis3.1. Degradation model for FRP composites in hot/wet conditionBased on experimental data reported in [1], Zahur et al. [3] proposed a generalized model to charac-terize the degradation of constitutive matrix of matrix material under hygrothermal condition, which isexpressed asdCmdt=  c⌘ log ⇣1   T/Tg⌘ C0m or ddt (1   !) =  c⌘ log ⇣1   T/Tg⌘ (1   !) (4)where C0m is for undegraded material; c is the moisture concentration; ⌘ is a model parameter that isobtained from experiment data; T is the temperature; Tg is the glassy transition temperature; and t isthe exposure time. Thus, this degradation model is actually to get instantaneous temperature T (t) andmoisture concentration c(t), and they are obtained from transient moisture di usion and heat conductionanalyses.3.2. Computational homogenization for multi-physics problemsOwing to the multi-scale architecture of composite materials, homogenization method should be usedto estimate the e ective properties of composites. In the present paper, the multi-scale computationalhomogenization method was used to estimate the e ective elastic and physical properties. Thermal anddi usion homogenization were conducted to get the e ective conductivity and di usivity, respectively.These were then supplied to transient heat conduction and moisture di usion analyses to calculate theinstantaneous temperature and moisture concentration for Eq. (4). Finally, the degraded elastic propertiesof constituentmaterialswere input to themechanical homogenization to get the e ective elastic properties.In the finite element context, the mechanical homogenization is expressed as"Kµ PTP 0# (u )=(0D"¯)orfKˆg {uˆ} = (Fˆ) . (5)where   is the Lagrangian vector, "¯ is the prescribed or given strain, and P and D are constraint matrixand global coordinate matrix.3623.3. Uncertainty propagation with the use of perturbation techniqueConsidering material properties as random variables, the sti ness matrixfKˆgand the nodal displacementvector {uˆ} in Eq. (5) are thus stochastic functions. According to the perturbation technique, stochasticfunction can be approximated by Taylor series expansion. In the present study, only the first orderexpansion is needed as the first order derivatives of structural responses are required in Eq. (3). Byexpanding stochastic functions in the form of (b) =  (b¯) + ✏nXi=1fDbi (b¯)g bi, (6)substituting them into Eq.(5) and equating terms of equal orders of ✏ , we arrive at the following zeroth-and first-order equations: fKˆg {uˆ} = (Fˆ) (7)nXp=1(fKˆg (Dbp uˆ)+fDbp Kˆg {uˆ}) = 0 (8)In Eq. (5), the block related to sti ness matrix,fKµg, of the microstructure is function of materialproperties. It and its first-order partial derivative can be expressed asKµ =Z⌦sµBTCµBdV, andfDbpKµg=Z⌦sµBTfDbpCµgBdV, (9)where B is the strain-displacement matrix, Cµ is the constitutive matrix of constituent material, andfDbpCµgis its first-order partial derivative. Computing Eqs.(7) and (8) successively, the compactdisplacement vector {uˆ} and its first order partial derivative (Dbp uˆ) can be obtained. These were thenused to calculated the e ective constitutive matrix and its derivatives according to C¯ =  ¯"¯ (see [4]for details of the derivation). Once the e ective constitutive matrix for the composite is obtained, thestochastic structural responses at macro level can be calculated by introducing a perturbation-basedstochastic finite element method, and these are input to Eq. (3).4. Numerical exampleA fibre reinforced polymer composite plate is considered in this section to illustrate the time-dependentreliability analysis scheme. The geometry of the plate is shown in Fig 1a. For the macro-level thermalproblem, a temperature of 80°C is applied to the top and bottom surfaces, and constant heat flux is appliedto the left and right surfaces. Similarly, for the moisture transport problem, a constant concentration of 1,which represents 100% relative humility, is applied to the top and bottom surfaces, and constant moistureflux is applied to the left and right surfaces. For the macro-mechanical analysis, a uniform pressure of1000 MPa is applied along the upper and lower surfaces in the vertical direction to simulate uniaxialtension state. Considering the symmetry of the geometry and boundary conditions for heat transfer,moisture transport and mechanical analysis, only 1/8 of the structure, highlighted in Fig. 1a, needs to bemodelled. The plate is made of glass/epoxy plain weave textile composite (see microstructure in Fig. 1b)with elastic and physical properties indicated in [3].The multi-scale analysis for heat conduction and moisture transport problems were conducted first toget the e ective heat conductivity and moisture di usivity required for performing macro level heatconduction and moisture di usion analyses. The calculations were conducted in a time interval of 10days, and a period of 500 days was considered. Thus, a total of 51 times of multi-scale multi-physicscalculation were conducted. Using these 51 instantaneous temperature and moisture concentration fields,a series of degradation parameter field was computed by Eq. (4). Then the mechanical computationalhomogenization was applied to estimate the e ective mechanical properties. According to preliminary363study at initial stage, applied load, longitudinal ply strength and longitudinal Young’s modulus are themost important parameters in reliability analysis of the considered structures. These three parameterswere considered as random variables in the time-dependent reliability calculation, and Tsai-Wu failuretheory was used to establish the LSF. Finally, the evolution in time of the reliability index is plotted inFig. 2. It can be seen that the reliability index decreases about 11% after 500 days degradation.(a) Plate(b) MicrostructureFigure 1: FRP plate and its mi-crostructure0 100 200 300 400 5002.82.852.92.9533.053.13.153.2Time t (in days)Reliability indext β  Beta (FORM)Figure 2: Evolution in time of the reliability index5. ConclusionsOn-going research and early results on the durability of fibre reinforced polymer composite structures,which is investigated by time-dependent reliability analysis, are presented in this paper. The time depen-dent reliability calculation is realized by integrating a multi-scale finite element reliability method witha hygro-thermo-mechanical model. A numerical study is carried out to demonstrate the applicability ofthe proposed scheme through the calculation of the evolution in time of the probability of failure.AcknowledgementsThe authors gratefully acknowledge the financial support provided for this study by the UK Engineeringand Physical Sciences Research Council (EPSRC) under grant reference EP/K026925/1.References[1] S. A. Grammatikos, B. Zafari, M. C. Evernden, J. T. Mottram, J. M. Mitchels, Moisture uptakecharacteristics of a pultruded fibre reinforced polymer flat sheet subjected to hot/wet aging, PolymerDegradation and Stability 121 (2015) 407–419.[2] S. A. Grammatikos,M. C. Evernden, J. M.Mitchels, B. Zafari, J. T.Mottram, G. C. Papanicolaou, Onthe response of hygrothermal aging of pultruded FRPs used in the civil engineering sector, Materials& Design In press.[3] Z. Ullah, L. Kaczmarczyk, S. A. Grammatikos, M. C. Evernden, C. J. Pearce, Multi-scale compu-tational homogenization to predict the long-term durability of composite structures, Computers &Structures Under review.[4] X.-Y. Zhou, P. D. Gosling, C. J. Pearce, Z. Ullah, L. Kaczmarczyk, Perturbation-based stochas-tic multi-scale computational homogenization method for woven textile composites, InternationalJournal of Solids and Structures 80 (2016) 368–380.364

Multi-scale finite element based time-dependent reliability analysis for laminated fibre reinforced composites.

Enlighten: Publications

Zhou, XY

Gosling, PD

Pearce, CJ

Kaczmarczyk, L

Queen's University Belfast Research Portal

Multi-scale finite element based time-dependent reliability analysis for laminated fibre reinforced composite

https://pure.ulster.ac.uk/ws/files/11630497/ACME2016.pdf

Multi-scale finite element based time-dependent reliability analysis for laminated fibre reinforced composites.

Abstract

Similar works

Full text

Available Versions

Enlighten

Ulster University's Research Portal

Enlighten: Publications

Queen's University Belfast Research Portal