The impact of alloying on the performance of β-Cu₂V₂O₇ photoanodes was investigated using inkjet printing of composition libraries containing 1,809 Cu₂V₂O₇-based photoanodes. Six elements (Zr, Ca, Hf, Gd, La, and Lu) were alloyed and pairwise co-alloyed at concentrations up to 7 at % into Cu-rich, stoichiometric, and Cu-deficient host Cu₂V₂O₇. A 1.7-fold increase in oxygen evolution photocurrent in pH 9.2 electrolyte was obtained by alloying Ca into β-Cu₂V₂O₇. Experiments employing a hole scavenger to better characterize bulk charge separation and transport revealed a 2.2-fold increase in photoactivity via alloying with Hf, Zr, and La, which increased to 2.7-fold upon co-alloying these elements with Ca. Concurrent with increased photoactivity is substantially decreased photon absorption between 1.5 and 2 eV, a range reported to coincide with high exciton absorption in β-Cu₂V₂O₇, motivating further exploration of whether these co-alloy compositions may destabilize the excitonic state that appears to have limited performance to date