CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Structure of a pentacene monolayer deposited on SiO<inf>2</inf>: Role of trapped interfacial water
Authors
,
J Bessette
+8 more
RL Headrick
A Kazimirov
GG Malliaras
AC Mayer
B Wang
Y Wang
S Wo
H Zhou
Publication date
23 November 2006
Publisher
Abstract
In situ synchrotron x-ray reflectivity is used to probe the early stages of pentacene growth in real time, under conditions relevant to the fabrication of organic thin film transistors. The results reveal that there is an interfacial water layer initially present on the Si O2 substrate and that this water layer is still present at the interface after the deposition of a pentacene thin film. The thickness of the trapped interfacial water layer does not significantly change subsequent to film deposition, even after exposure to atmospheric pressure or during vacuum annealing at 70 °C. However, a water layer is observed to form on the free surface of pentacene after sufficient exposure to water vapor, and the thickness of this layer can be reduced by subsequent vacuum annealing. These observations are correlated with organic thin film transistor mobilities measured at atmospheric pressure versus under vacuum. © 2006 American Institute of Physics
Similar works
Full text
Available Versions
CUED - Cambridge University Engineering Department
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:generic.eprints.org:928785...
Last time updated on 15/07/2020