Room temperature photoresponse in the mid-infrared spectral region is demonstrated from InAsSbN/InAs multi-quantum well photodiodes grown by nitrogen plasma assisted molecular beam epitaxy. The structural quality of the InAsSbN MQWs was ascertained in situ by reflection high energy electron diffraction and ex situ by high resolution x-ray diffraction and photoluminescence measurements. The extended long wavelength photoresponse is identified to originate from the electron–heavy hole (e1–hh1) and electron–light hole (e1–lh1) transitions in the InAsSbN MQW, with a cut off wavelength ~4.20 µm and peak detectivity D *  =  1.25  ×  109 cm Hz1/2 W−1

A Krier

de la Martin M

Ding-Kang S

Godenir A

Latkowska M

M de la Mare

M Kesaria

Rogalski A

Crossref

Journal of Physics D Applied Physics

Room temperature mid-infrared InAsSbN multi-quantum well photodiodes grown by MBE

Kesaria, M.

de la Mare, M.

Krier, A.

Online Research @ Cardiff

Journal of Physics D: Applied PhysicsPAPER • OPEN ACCESSRoom temperature mid-infrared InAsSbN multi-quantum well photodiodes grown by MBETo cite this article: M Kesaria et al 2016 J. Phys. D: Appl. Phys. 49 435107 View the article online for updates and enhancements.Recent citationsReducing N 2 O induced cross-talk in aNDIR CO 2 gas sensor for breath analysisusing multilayer thin film opticalinterference coatingsLewis Fleming et al-This content was downloaded from IP address 131.251.254.231 on 09/10/2018 at 12:211 © 2016 IOP Publishing Ltd Printed in the UKIntroductionPhotodetectors operating in the mid-infrared spectral range (3–5 µm) are of technological importance due to their mili-tary applications in infrared countermeasures and night vision as well as many civil applications, including atmospheric pollution monitoring, optical spectroscopy and medical diag-nostics. Mercury cadmium telluride (MCT) photodetectors are commonly used for some of these applications together with InGaAs, InSb, InAsSb [1] and InAsSbP [2]. MCT alloys have a small electron effective mass (~0.009 m0) resulting in unde-sirable dark currents due to tunnelling and require cooling. These alloys also suffer from compositional non-uniformity which compromises the detector spectral response over large areas [3–5]. Access to mid-infrared wavelengths can also be achieved using alternative III–V based material systems such as InAsN, where the addition of small amounts (<1%) of nitrogen into InAs has been found to substantially reduce the band gap and allow tailoring of the detection wavelength [6–9]. Research into dilute nitride materials can give insight into fundamental physics and also has potential for the devel-opment of new high performance detectors and large-format focal plane arrays [10, 11].Room temperature electroluminescence (EL) at a peak wavelength ~3.7 µm was demonstrated earlier from type II InAsSb/InAs multi-quantum well (MQW) light- emitting diodes (LEDs) [12]. The introduction of nitrogen into InAsSb quantum wells changes the band alignment from type-II to type-I due to an increase in the electron confine-ment and bandgap reduction, with no excess strain. The sur-factant effect of Sb during growth enhances the crystalline and optical quality of InAsSbN, whereas the adjustment of Sb and N contents enables lattice matching to InAs and strain tailoring in the QW. Previously, we have reported good quality InAsSbN alloys, InAsSbN p-i-n diodes emit-ting near 4.0 µm at room temperature [13–15], InAsSbN MQW [16] and InAsSbN MQW LEDs emitting at 3.6 µm (4 K) [17]. More recently InAsN and InGaAsN MQW imple-mented on InP substrate have been shown to enable dilute nitride mid-infrared laser diodes [18]. InAsSbN quantum wells [19] and laser diodes [20] have also been reported elsewhere in the literature, but there are very few studies Journal of Physics D: Applied PhysicsRoom temperature mid-infrared InAsSbN multi-quantum well photodiodes grown  by MBEM Kesaria, M de la Mare and A KrierPhysics Department, Lancaster University, Lancaster, LA1 4YB, UKE-mail: m.kesaria@lancaster.ac.ukReceived 31 July 2016, revised 27 August 2016Accepted for publication 5 September 2016Published 4 October 2016AbstractRoom temperature photoresponse in the mid-infrared spectral region is demonstrated from InAsSbN/InAs multi-quantum well photodiodes grown by nitrogen plasma assisted molecular beam epitaxy. The structural quality of the InAsSbN MQWs was ascertained in situ by reflection high energy electron diffraction and ex situ by high resolution x-ray diffraction and photoluminescence measurements. The extended long wavelength photoresponse is identified to originate from the electron–heavy hole (e1–hh1) and electron–light hole (e1–lh1) transitions in the InAsSbN MQW, with a cut off wavelength ~4.20 µm and peak detectivity D*  =  1.25  ×  109 cm Hz1/2 W−1.Keywords: dilute nitride, InAsSbN, MBE, photodiodes(Some figures may appear in colour only in the online journal)M Kesaria et alPrinted in the UK435107JPAPBE© 2016 IOP Publishing Ltd201649J. Phys. D: Appl. Phys.JPD0022-372710.1088/0022-3727/49/43/435107Paper43Journal of Physics D: Applied PhysicsIOPOriginal content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.0022-3727/16/435107+6$33.00doi:10.1088/0022-3727/49/43/435107J. Phys. D: Appl. Phys. 49 (2016) 435107 (6pp)M Kesaria et al2on dilute nitride photo-detectors operating in the 2–5 µm spectral range [21–23].In this work, we demonstrate InAsSbN MQW photodiodes grown on InAs substrate by plasma assisted molecular beam epitaxy. The structural quality of the InAsSbN MQWs was ascertained by high resolution x-ray diffraction and photolu-minescence measurements. Room temperature photoresponse was observed in the mid-infrared, with a cut-off wavelength near 4.20 µm and a peak detectivity of D*  =  1.25  ×  109 cm Hz1/2 W−1. The extended long wavelength response was iden-tified to originate from confined states of the dilute nitride MQW (e1–hh1 and e1–lh1) which is in good agreement with calculated values.ExperimentA VG-V80H molecular beam epitaxy (MBE) reactor was used to grow the InAsSbN quantum wells on n-InAs (0 0 1) substrates, as well as the complete MQW photodiode device structure. During this growth phase, in situ characteriza-tion was performed by reflection high energy electron dif-fraction (RHEED). In, Al and Ga fluxes were provided by Knudsen thermal effusion cells. The As2 and Sb2 was gen-erated from valved cracker cells and the atomic N flux by a Veeco Uni-bulb radio frequency plasma nitrogen source. The nitrogen flux was generated using a load power of 210 W and a nitrogen beam equivalent pressure (BEP) ~ 7.0  ×  10−7 mbar. BEP ratio of As/Sb  =  2.6 and As/N  =  3.7 (BEP of Sb ~ 1.1  ×  10−6 mbar, BEP of N2 ~ 7.0  ×  10−7 mbar and As ~ 2.6  ×  10−6 mbar). To optimize N incorporation into the MQW the minimum As flux was used during the growth of the InAs layers, since the adatom sites are more favourable for As than for N incorporation. In order to ascertain surface cleanliness and monitor crystalline quality, surface recon-structions were monitored by RHEED. Typical (2  ×  4) and (1  ×  3) RHEED patterns shown in figure 1(a) were observed during the growth in [0 1 1] and [0 1 1] directions for the InAs and InAsSbN surfaces, respectively. The substrate temperature was measured using an infrared pyrometer and back-calibrated by monitoring surface reconstruction trans-itions at a fixed As flux. The substrate preparation and oxide desorption was carried out in the conventional manner in the growth chamber. To desorb oxide from the InAs substrate required heating gradually up to 520 °C under As flux, (until a weak  ×  3 RHEED pattern transformed to the brighter  ×  2 pattern) [24]. To obtain abrupt quantum well interfaces and realize a low residual carrier concentration ~2  ×  10 17 cm−3 in the MQW, the surface was exposed to Sb for 3s (Sb flux ~3  ×  10−7) prior to InAsSbN quantum well growth and before the InAs barrier growth the surface was exposed to As (flux ~4  ×  10−6 mbar) for 20 s. The RHEED pattern was clearly 1  ×  3 at the beginning of the active region and transformed to 2  ×  4 under As2 flux, suggesting an efficient As–Sb exchange Figure 1. (a) Typical 2  ×  4 and 1  ×  3 RHEED patterns for InAs and InAsSbN surface observed during the growth in the [0 1 1] and the [0 1 1] direction; (b) schematic details of the MQW structure used in the photodiode active region and (c) the complete photodiode structure, each containing 10 InAsSbN quantum wells.J. Phys. D: Appl. Phys. 49 (2016) 435107M Kesaria et al3reaction and excess Sb removal from the surface. The struc-tural quality and material composition was determined using high resolution x-ray diffraction (HRXRD) measurements. The resulting wafers were processed into 1 mm diameter mesa-etched diodes using standard photolithographic and wet etching techniques before mounting onto TO-46 headers. Photoluminescence (PL) and electroluminescence (EL) mea-surements were performed using an Oxford Instruments vari-able temperature continuous flow He cryostat. The emitted radiation was collected using CaF2 lenses and focused into a 0.3 m Bentham M300 grating monochromator. For EL the devices were tested at 1 kHz using a 50% duty cycle exci-tation and the radiation was detected using a cooled (77 K) InSb photodiode detector and a Stanford Research (SR850) digital lock-in amplifier. The photo-response was measured using an Oriel Instruments 80007 silicon carbide source with a 1200 K colour temperature that was chopped at 175 Hz.A schematic representation of the MQW structure and the corresponding photodiode detector is shown in figures  1(b) and (c), respectively. The MQW structure consists of ten InAs0.942Sb0.050N0.008 quantum wells, each 10 nm wide with 25 nm InAs barriers, grown on InAs substrate. For the pho-todiode a 0.5 µm Te doped InAs layer is grown on InAs at 490 °C (1 µm h−1 growth rate) which is followed by ten 10 nm InAs0.942Sb0.050N0.008 quantum wells with 25 nm InAs bar-riers (0.5 µm h−1 growth rate) at lower substrate temperature 410 °C. The growth temperature is raised to 490 °C for the growth of the 30 nm undoped Al0.90Ga0.10As0.21Sb0.79 electron Figure 2. High resolution x-ray diffraction rocking curves (black) and simulated XRD patterns (blue dotted) of (a) the MQW active region and (b) the complete photodiode structure.J. Phys. D: Appl. Phys. 49 (2016) 435107M Kesaria et al4blocking barrier above the active region and finally capped by 500 nm thick Be-doped InAs.Results and discussionThe incorporation of N or Sb into InAs layers is known to introduce tensile or compressive strain respectively. Therefore, addition of 0.8% N to InAs0.95Sb0.05 MQW reduces compres-sive strain from 0.5% to 0.2% allowing strain-balancing and we used this in the growth of the InAsSbN MQW structure and photodiode used here. The corresponding HRXRD rocking curves are shown in figures 2(a) and (b), respectively. The peak at 858 arc seconds corresponds to the Al0.90Ga0.10As0.21Sb0.79  layer in the photodiode. The diffraction pattern of both struc-tures has a distinct zero order peak and a few high-order satel-lite peaks. The absence of higher angle satellite peaks can be due to atomic level roughness at the interface between the well and barrier. In our earlier work we have shown that in InAsSbN/InAs MQWs the interface between the well and barrier can have roughness up to  ±2 nm [17]. InAsSbN epilayers (1 µm thick) grown on InAs substrate in different Sb and N condi-tions were used to determine Sb and N composition [14–16]. Simulation of the structures was done using Bede RADS soft-ware which is based on the dynamical scattering theory of dif-fraction. The solid lines (black) are experimental results and the dashed lines (blue) are simulated data. The derived thick-nesses of the perfectly strain balanced InAsSbN well and InAs barrier are approximately 10 nm and 25 nm, respectively.Figure 3 shows (a) the 4 K PL emission spectrum and (b) the 300 K EL spectrum. The experimental PL and EL data were de-convoluted by fitting Gaussian peaks. For the 4 K PL these peaks are centred at 0.340 and 0.355 eV, which is approxi-mately in agreement with the calculated e1–hh1 and e1–lh1 QW transitions, respectively. The calculation of the trans ition energies was done using a Schrodinger solver within an effec-tive mass approximation, taking into account N-induced band anti-crossing effects, coupling constants and strain [16]. The difference between calculated and experimental values orig-inates from uncertainties in N and Sb content and also the effective masses within the QW [25]. The room temperature EL spectrum shown in figure 3(b) was similarly de-convoluted into three peaks which are centred at 0.318 eV, 0.349 eV and 0.396 eV. The first being attributed to e1–hh1 QW transition, while the peaks at 0.349 eV and 0.396 eV arises from recom-bination taking place in the intrinsic n0 InAs barriers and n+ InAs, respectively.Figure 4 compares the room temperature photoresponse of (a) an InAs photodiode (with an InAsSbP window) [26], (b) the InAsSbN MQW photodiode, and (c) the electrolumines-cence from the InAsSbN MQW diode. The photoresponse of the InAsSbN MQW photodiode extends from 1.10 to 4.20 µm having an extended cut off at 4.20 µm compared with the cut off wavelength for InAs at 3.88 µm. The maximum of the electroluminescence spectrum at 3.57 µm is 0.63 µm lower than the cut-off of the MQW diode photoresponse.Current–voltage (I–V) curves were obtained at temperatures 20 K–300 K for the InAsSbN MQW photodiode. Figure 5(a) shows a semi-logarithmic plot of the I–V curves acquired at 20, 160 and 300 K using a bias in the range  −0.4 to 0.8 V from which the corresponding diode series resistance is estimated Figure 3. (a) The 4 K PL spectra and (b) 300 K EL spectra in black. The de-convoluted Gaussian peaks; e1–hh1 (red), e1–lh1 (blue), n0 InAs (brown) and n+ InAs (green) are labelled accordingly.Figure 4. The room temperature logarithmic plots of (a) photoresponse from a bulk InAs photodiode with an InAsSbP window, (b) the InAsSbN MQW photodiode and (c) electroluminescence from the InAsSbN MQW diode (at injection current 100 mA). The photoresponse spectra contain features due to atmospheric absorption from water vapour in the optical path around 2.7 µm.J. Phys. D: Appl. Phys. 49 (2016) 435107M Kesaria et al5as ~2.5 Ω and the ideality factor (β) ~1.56 below 150 K. The diode reverse leakage current decreased from 2 mA to 0.7 mA with a reduction in temperature from 300 K to 20 K. To understand the current conduction mechanisms an Arrhenius plot of zero bias resistance area (R0A) was extracted and is shown in figure 5(b). The R0A values grow exponentially with decreasing temperature, but the growth rate is different at high and low temperatures. The straight lines show the fits obtained using the energy (E  =  0.29 eV) in the exponent (expE/βkT) which is close to the e1–hh1 transition of the InAsSbN (N ~ 1%) MQWs. The results are consistent with diffusion current (β ~ 1) in the 200–300 K temperature range. At low temper-atures generation recombination current dominates consistent with β ~ 2. The specific (peak) detectivity of the InAsSbN MQW photodiode was determined as D*  =  1.25  ×  109 cm Hz1/2 W−1 at 300 K for the mesa etched 1 mm diameter diodes in this work, using the Johnson noise limited equa-tion [27]. This is comparable with previously reported InAsSb (InAsSbP) photodiodes at 300 K [1–2] and is encouraging since the MQW diodes are not yet optimized or anti-reflection coated. The valence band offsets (62 meV) of the MQWs are small enough to allow the photogenerated carriers to escape at 300 K and the number of QW can be increased further to increase absorption using strain balancing. Consequently, this material system shows promise as the addition of N provides an additional freedom in tailoring the band structure within a type I QW system at longer wavelengths. To improve device quality, further work is in progress to reduce the active region residual carrier concentration and improve the MQW inter-face quality as well as extend the wavelength range by the introduction of more nitrogen.ConclusionWe have demonstrated uncooled InAsSbN/InAs MQW photo-diodes, grown strain balanced on InAs by MBE, which exhibit a photoresponse in the mid-infrared spectral range at 300 K. The structural and optical quality were ascertained by high resolution x-ray diffraction and photo-/electroluminescence. The diodes exhibit responsivity in the mid infrared spectral region with an extended long wavelength response, which is identified to originate from the InAsSbN e–hh1 and e–lh1 trans itions and is in agreement with calculated values. The photodiodes exhibit a cut-off wavelength of near 4.2 µm at room temperature with a specific detectivity, D*  =  1.25  × 109 cm Hz1/2 W−1 at 300 K. Since InAsSbN enables strain- balancing on InAs the dilute nitride alloys offer some addi-tional freedom in tailoring long wavelength photodetectors.AcknowledgmentsThe authors are grateful to the Engineering and Physical Sci-ence Research Council (EPSRC) for financial support (grant EP/J015849/1). The data in the figures for this manuscript are openly available from Lancaster University data archive at https://dx.doi.org/10.17635/lancaster/researchdata/98References [1] Gao H H, Krier A and Sherstnev V V 2000 Appl. Phys. Lett. 77 872 [2] Krier A and Suleiman W 2006 Appl. Phys. Lett. 89 083512 [3] Rogalski A 2005 Rep. Prog. Phys. 68 2267 [4] Rogalski A 2012 Opto-Electron. Rev. 20 279 [5] Rogalski A 2010 Opto-Electron. Rev. 18 478 [6] Nishikawa A, Katayama R, Onabe K and Shiraki Y 2003  J. Cryst. Growth 251 427 [7] Ding-Kang S, Hao-Hsiung L, Li-Wei S, Tso-Yu C and Yang T R 2003 Japan. J. Appl. Phys. 42 375 [8] Bi W G and Tu C W 1997 Appl. Phys. Lett. 70 1608 [9] Chang A S, Zech E S, Kim T W, Lin Y H, Mawst L J and Goldman R S 2014 Appl. Phys. Lett. 105 142105 [10] Veal T D, Piper L F J, Jefferson P H, Mahboob I, McConville C F, Merrick M, Hosea T J C, Murdin B N and Hopkinson M 2005 Appl. Phys. Lett. 87 182114 [11] Kuroda M, Katayama R, Nishio S, Onabe K and Shiraki Y 2003 Phys. Status Solidi c 0 2765Figure 5. (a) The I–V curves acquired at 20 K, 160 K and 300 K from the InAsSbN MQW photodiode (data for other temperatures omitted for clarity); and (b) the zero bias resistance area (R0A) versus reciprocal of temperature plot derived from the I–V measurements for the same InAsSbN diode. The straight lines correspond to exp(0.29/kT) and exp(0.29/2kT).J. Phys. D: Appl. Phys. 49 (2016) 435107M Kesaria et al6 [12] Krier A, Stone M, Zhuang Q D, Liu P-W, Tsai G and Lin H H 2006 Appl. Phys. Lett. 89 091110 [13] Zhuang Q, Godenir A, Krier A, Tsai G and Lin H H 2008 Appl. Phys. Lett. 93 121903 [14] Latkowska M et al 2016 J. Phys. D: Appl. Phys. 49 115105 [15] Godenir A 2008 Novel dilute nitride semiconductor materials for mid-infrared applications PhD Dissertation Lancaster University, Lancaster (available from: Lancaster E-prints) [16] de la Martin M, Carrington P J, Wheatley R, Zhuang Q, Beanland R, Sanchez A M and Krier A 2010 J. Phys. D: Appl. Phys. 43 345103 [17] Carrington P J, de la Mare M, Cheetham K J, Zhuang Q and Krier A 2011 Adv. OptoElectron. 2011 145012 [18] Wheatley R, Kesaria M, Mawst L J, Kirch J D, Kuech T F, Marshall A, Zhuang Q D and Krier A 2015 Appl. Phys. Lett. 106 232105 [19] Shono T, Mizuta S and Kawamura Y 2013 J. Cryst. Growth 378 69 [20] Kawamura Y and Inoue N 2007 J. Cryst. Growth  301–2 963 [21] Tan K H et al 2007 Appl. Phys. Lett. 90 183515 [22] Luna E, Hopkinson M, Ulloa J M, Guzmán A and Muñoz E 2003 Appl. Phys. Lett. 83 3111 [23] Aina L, Hier H, Fathimulla A, Lecates M, Kolodzey J, Goossen K, Coppinger M and Bhargava N 2009 Infrared Phys. Technol. 52 310 [24] Bhatnagar K, Rojas-Ramirez J, Caro M, Contreras R, Henninger B and Droopad R 2015 J. Cryst. Growth  425 16 [25] Patanè A et al 2009 Phys. Rev. B 80 115207 [26] Krier A et al 2015 Infrared Phys. Technol. 73 126 [27] Dennis P N J 1986 Photodetectors (New York: Plenum)J. Phys. D: Appl. Phys. 49 (2016) 435107

https://orca.cardiff.ac.uk/id/eprint/115530/1/Kesaria_2016_J._Phys._D__Appl._Phys._49_435107.pdf

Room temperature mid-infrared InAsSbN multi-quantum well photodiodes grown by MBE

Abstract

Similar works

Full text

Available Versions

Crossref

Online Research @ Cardiff