The mango kernel starch (MKS) - glycerol (GLY) films were prepared via solution
casting method. The blend ratio of MKS and GLY was fixed at 1:1 wt. %, while the
composition of oregano essential oil (OEO) was varied from 0, 0.3, 0.4, 0.5, and 0.6 wt. %. In
this study, the effect of OEO on mechanical, morphological and biodegradable properties of
MKS - GLY films were evaluated. From the analysis, the optimum tensile strength of MKS –
GLY film was obtained at 1.10 MPa, while the addition of 0.4 wt. % OEO to MKS – GLY film
resulted in optimum tensile properties, which give a smooth surface with less voids, as
presented in the micrographs by scanning electron microscope (SEM). Moreover, the addition
of 0.4 wt. % OEO to MKS – GLY film exhibited minimum weight loss during soil burial test,
thus confirmed the function of OEO as an antimicrobial agent