Eleven different Fusarium species were isolated from various infected plant materials and screened to select a potential species for the synthesis of silver nanoparticles. All the isolates were identified on the basis of cultural and microscopic characteristics using Fusarium identification keys. For the confirmation of preliminary identified isolates of Fusarium species, online BLAST analysis was carried out. All the eleven species demonstrated the ability for synthesis of silver nanoparticles. This was confirmed by UV-Vis spectroscopy, which gave characteristic peak around 420 nm. Further confirmation of silver nanoparticles was carried out using nanoparticles tracking analysis (NTA), zeta potential, photon correlation spectroscopy (PCS), powder X-ray diffractometry (XRD) and transmission electron microscopy (TEM). The smallest size of silver nanoparticles was synthesized by F. oxysporum (3-25 nm) and largest size silver nanoparticles were synthesized by F. solani (3-50 nm).Onze diferentes espécies de Fusarium foram isoladas a partir de vários materiais vegetais infectados e selecionados para escolher uma espécie potencialmente importante para a síntese de nanopartículas de prata. Todos os isolados foram identificados com base nas características de cultivo e microscópicas usando as chaves de identificação de Fusarium. Para a confirmação e identificação preliminar dos isolados de espécies de Fusarium, a análise BLAST on-line foi utilizada. Das espécies isoladas onze mostraram a capacidade para a síntese de nanopartículas de prata. A síntese de nanopartículas de prata foi confirmada por espectroscopia de UV-Vis que monstrou um pico característico em torno de 420 nm. Além disso, a confirmação da síntese de nanopartículas de prata foi realizada utilizando a análise de rastreamento de nanoparticulas (nanoparticle tracking analysis-NTA), medidas de potencial zeta, espectroscopia de correlação de fótons (PCS), difratometria de raios X de pó (XRD), e microscopia eletrônica de transmissão (TEM). As menores nanopartículas de prata foram sintetizadas por F. oxysporum (3-25 nm), enquanto as maiores foram obtidas com F. solani (3-50 nm).19741982Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq