Studi awal tentang fisibilitas daur ulang aktinida minor (MA) tanpa melibatkan plutonium dalam reaktor air mendidih (boiling water reactor, BWR) telah dilakukan. Hasil yang diperoleh menunjukkan bahwa dengan menaikkan konsentrasi fisil MA dalam bahan bakar mixed oxide (MOX) dan/atau memperkecil fraksi hampa maka faktor multiplikasi efektif pada awal siklus akan naik juga, tetapi kenaikan ini belum cukup untuk membuat reaktor kritis. Disisi lain memperkecil void fraction akan menaikkan ayunan reaktivitas yang pada akhirnya akan menurunkan faktor keselamatan dari reaktor.

Forsten, Jarl

Saario, Timo

Törrönen, Kari

Wallin, Kim

An integral part of the safety assessment of nuclear pressure vessels and piping is the quantitative estimation of defect growth in both a stable and an unstable manner during service. This estimation is essential for determining whether any defect detected during inspection should be repaired or whether the size of the defect even after its expected growth is small enough to leave the integrity of the vessel unaffected.The most important stable defect growth mechanism is that of environmentally assisted cyclic crack growth. Recent results indicate that it is markedly affected by sulphur content and/or manganese sulphide morphology and distribution. This implies that an essential improvement in component safety has been gained by currently applied steelmaking practices, which result in extra low sulphur content, generally below 0·010 wt.%, and in the round shape and small size of inclusions through, e.g. calcium treatment, hence considerably reducing the effect of the environment on crack growth rate. This further implies that the ASME Section XI reference curves for environmentally accelerated cyclic crack growth are conservative for steels produced by current steelmaking practices.The ASME Section XI applies predominantly linear elastic fracture mechanics to assess the effects of cracks on the integrity of nuclear power plant components. Unstable linear elastic fracture often propagates by a cleavage mechanism. The cleavage fracture process has recently been shown to be of a statistical nature in both ferritic and bainitic steels. The carbide size distribution plays a dominant role in controlling the fracture toughness of these steels. A cleavage fracture model has been developed, by which both the expectance value and the probability limits of the fracture toughness, , can be predicted. The probability limits given by the model are shown to be consistent with the experimental observations. The application of the model to the data on which the ASME Section XI reference fracture toughness curve is based indicates that the reference curve is slightly unconservative

STUDI TENTANG FISIBILITAS DAUR ULANG AKTINIDA MINOR DALAM BWR

Abstract

Similar works

Full text

Available Versions

VTT Research System

Badan Tenaga Nuklir Nasional: Jurnal BATAN

VTT Research System

Jurnal Sains dan Teknologi Nuklir Indonesia

VTT Research System

VTT Research System