Combined EELS, CL and STEM imaging are used to characterize and study Y2O3:Eu to confirm the variation in CL properties and photo-luminescent properties observed.  The synthetic procedures used have facilitated this material to manifest a strong blue emission at low temperature with the expected red emission dominating at room temperature

Engelsen, D

Fern, G

Howkins, A

Ireland, T

Lipman, A

Marsh, P

Silver, J

Brunel University Research Archive

 Blue and red cathodoluminescent emission of Y2O3:Eu phosphor studied as a function of temperature in a transmission electron microscope  George R. Fern, Anthony Lipman, Jack Silver, Ashley Howkins, Terry G. Ireland, Paul Marsh and Daniel den Engelsen Wolfson Centre for Materials Processing incorporating the Centre for Phosphors and Display Materials, Institute of Materials and Manufacturing, Brunel University London, Uxbridge, Middlesex, UB8 3PH, UK  Keywords: Cathodoluminescence, Transmission Electron Microscopy, Y2O3Eu, Electron beam reduction  ABSTRACT Combined EELS, CL and STEM imaging are used to characterize and study Y2O3:Eu to confirm the variation in CL properties and photo-luminescent properties observed.  The synthetic procedures used have facilitated this material to manifest a strong blue emission at low temperature with the expected red emission dominating at room temperature.  1. INTRODUCTION We have previously shown how cathodoluminescence can be used inside the transmission electron microscope to study phosphors such as Y2O2S:Tb,1 Gd2O2S:Tb2 and the quantum dots, CdSe/ZnCdS3 and dot-in-rods CdSe/CdS4 which have wide ranging applications in scintillation phosphors through to the latest developments in high information content television displays.  In order to develop improved synthetic techniques for the fabrication of phosphors it is important to understand the impact of the procedure used and the effect of the materials used to facilitate this.  In this work we will show the effect of solvent in synthesizing Y2O3:Eu3+ and show how this has dramatically influenced the emission properties of the phosphor produced. In the class of rare earth phosphors europium has a unique position, because it can be divalent or trivalent in a host lattice. Both divalent and trivalent Eu phosphors enjoyed considerable industrial interests: BaAl2S4:Eu2+ as blue phosphor in thin film electroluminescent displays5 and Y2O3:Eu3+ as red phosphor in fluorescent lamps and projection cathode ray tubes (CRTs)6. The usual way to prepare Eu2+ phosphors is by annealing in a reducing atmosphere, while Eu3+ phosphors are normally prepared in oxidizing atmospheres, notably air. Besides these normal chemical synthesis methods it has been shown that certain oxygen containing crystals can be doped with Eu2+ by annealing in air7,8. In many oxygen containing crystals the Eu3+ dopant can be reduced to Eu2+ by exposure to high energy radiation such as UV9,10, X-rays11, E-rays12, J-rays12,13 , femtosecond laser pulses14 and electron beams15. A comprehensive theory on the role of the lattice does not exist; however, some properties are supposed to be important. One is the electronegativity difference between oxygen and the cation that is replaced by Eu3+. Another is the crystal structure, i.e. the coordination number of Eu3+ in the lattice and finally, the level of the charge transfer (CT) band, although, from the evidence available in the literature it cannot be concluded that a low CT level (as present in Y2O3:Eu3+) is enhancing the Eu3+ o Eu2+ reduction in oxygen containing crystals9,10,12,13.   2. EXPERIMENTAL Yttrium oxalate and europium oxalate in isopropanol (IPA) were mixed and transferred to a desiccator under vacuum to remove the IPA. The resulting powder with a Eu concentration of 6.37% was oven dried at 100oC.  Portions of the dried powder were fired at 1300oC for periods of time ranging from 0.5 hours to 3.5 hours.  The samples were characterised using bulk cathodoluminescence (CL) and Photoluminescence (PL) spectroscopy measurements which were carried out using a Bentham Instruments dual excitation and emission monochromator system. CL measurements were made whilst exciting a powder sample mounted onto an SEM stub inside a vacuum chamber with electron beam energies ranging from 1-3 kV impinging on the sample. A Pritchard PR880 photometer was used to measure the luminance.   All electron microscopy measurement were carried out (and CL STEM) at a temperature range of 30oC to -167oC) in a JEOL 2100F analytical TEM operated at 200 kV by dispersing the sample onto holey carbon coated copper grids.  STEM was carried out using a Gatan HAADF detector.  CL images were collected using a Gatan Vulcan™ system.  A Gatan Electron Energy Loss Spectrometer was used to map the position of the europium ions.   PHp1 - 2ISSN-L 1883-2490/22/0532 © 2015 ITE and SID IDW ’15       532 3. RESULTS AND DISCUSSION  The morphology of the particles produced manifest as large sheets of sintered ~100 nm sized particles as shown in figure 1.   Figure 2 1-7 fired at 1300oC and 7-8 fired at 950oC.  Luminance and observable colour of samples prepared under various conditions.    Figure 1 Annular dark field STEM image of Y2O3:Eu phosphor used in this study (Sample 1).  Under electron bombardment from 1kV to 3kV in a vacuum chamber, colours ranging from pink to blue were observed (figure 2).  Under ultra violet light (254nm), these phosphors gave a dull red luminescence with a weak blue emission below 400nm (see figure 3).  Figure 3 Photoluminescent spectrum of Sample 1. Red line shows a times 40 expansion from 380-420nm.   Figure 4 Panchromatic visible light image collected using the Vulcan photomultiplier tube.  In figure 4 the visible light emission from the particles is seen to be uniform across the cluster of particles which is consistent with the expected Sample no. Firing time (hours) Voltage (volts) 1 0.5 1000 1500 2500 3000 Cdm-2  3.83 10.00 22.2 29.60 Colour  violet violet violet violet 2 1.0 1000 1500 2500 3000 Cdm-2  5.75 11.8 25.2 31.2 Colour  violet violet violet violet 3 1.5 1000 1500 2500 3000 Cdm-2  6.91 13.50 27.60 34.10 Colour  pink/violet violet violet violet 4 2.0 1000 1500 2500 3000 Cdm-2  5.44 10.40 21.90 27.30 Colour  pink/violet violet violet violet 5 2.5 1000 1500 2500 3000 Cdm-2  7.07 12.50 25.70 31.80 Colour  pink  pink/violet violet violet 6 3.0 1000 1500 2500 3000 Cdm-2  6.92 13.20 26.30 30.80 colour  red  pink/ violet violet violet 7 3.5 1000 1500 2500 3000 Cdm-2  6.92 12.70 24..40 28.00 colour  pink/violet pink/ violet pink/ violet pink/ violet 8 2.0 1000 1500 2500 3000 Cdm-2  8.36 14.90 32.90 36.60 colour  violet violet violet violet 9 3.0 1000 1500 2500 3000 Cdm-2  4.29 8.59 17.20 20.60 colour  violet violet blue blue 533       IDW ’15 uniform emission from this material prepared via a homogeneous precipitation route and indicated by the uniform distribution of Eu ions seen in the EELS map in figure 5.    Figure 5 Thickness corrected Eu EELS map of particles showing the homogeneous distribution of Eu ions in Sample 1      Figure 6 (top) CL spectra as a function of temperature from +30oC to -167oC, (middle) CL spectrum at +20oC, (bottom) CL spectrum at -167oC.  In figure 6 the emission properties of the sample shown in figure 1 are presented.  At room temperature the sample manifests the expected Eu3+ emission with sharp line at 611 nm but in addition weak blue (394 nm) and deep red (773 nm) emission bands are observed.  On reducing the temperature these two bands become dominant whilst the red emission intensity at 611 nm remains unchanged.  These emission bands correspond to those expected for the emission due to Eu2+(4f65d to 4f7 transition)6 the position of which is highly dependent on the host lattice.  A plot of the CL emission intensity (Figure 7) over the linear portion gives an activation energy of 1280741 cm-1 at 394 nm and 66628 cm-1 at 773 nm.  This electron beam reduction has been previously documented in host lattices such as anhydrates, sulfates and fluorites.15  However we have not seen this behaviour in Y2O3:Eu3+ under normal synthesis using the urea precipitation method and a firing temperature around 1000oC. Figure 7 Arrhenius plot of the reciprocal intensity of the bands at 394 nm and 773 nm with trend lines showing the activation energies.  In figure 7 we have plotted the temperature dependence of the CL intensity spectra shown in figure 6.  The two activation energies found are very similar which indicates that these two emission bands are related to the Eu2+ state.  From this we find a small average activation energy of 0.057 eV.  It is possible that there are 2 processes describing the temperature dependence, however we do not have enough information to be confident in this conclusion.  To our knowledge this is the first time that this reduction of Eu3+ has been observed in the yttria lattice.  4. CONCLUSIONS The reduction of Eu3+ to Eu2+ in yttria host crystals under electron bombardment has not been observed earlier. At low temperature this reduction is much stronger than at room temperature. Furthermore, it was found that nanosized Y2O3:Eu3+ made by the urea synthesis or commercial micrometer-sized Y2O3:Eu3+ could not be reduced under electron bombardment. The usual factory process to produce commercial Y2O3:Eu3+ is the oxalate precipitation method without an         IDW ’15       534 intermediate step in IPA6. This step seems to be essential for the reduction of Eu3+. At this moment we don´t have an explanation for the observed reduction of Eu3+ in the Y2O3 lattice.  CL emission bands at 394 nm and 773 nm are shown to be related and assigned to Eu2+ in yttria.  5. AKNOWLEDGEMENTS We are grateful to the EPSRC and the TSB for funding the PURPOSE (TP11/MFE/6/I/AA129F; EPSRC TS/G000271/1), HTRaD (EP/L504671/1).  and CONVERTED (JeS no. TS/1003053/1) programs.   6. REFERENCES [1] J. Silver, X. Yan, G.R. Fern and N. Wilkinson, “Cathodoluminescence spectra of single Y2O3:Tb3+ nanometer sized phosphor crystals excited in a field emission scanning transmission microscope.” Proc. IDW, 823-826, (2013). [2] G.R. Fern, X. Yan, N. Wilkinson and J. Silver, “Cathodoluminescence Spectra of Single Gd2O2S:Tb3+ Nanometer Sized Phosphor Crystals Excited in a Field Emission Scanning Transmission Electron Microscope” Proc. IDW, 820-822, (2013). [3] G.R. Fern, J. Silver and S. Coe-Sullivan, “Cathodoluminescence and electron microscopy of red quantum dots used for display applications.” JSID, (2015) DOI: 10.1002/jsid.278. [4] G.R. Fern, J. Silver, T. Jochum, J.S. Niehaus, F. Schröder-Oeynhausen and H. Weller, “Red quantum rods under the electron microscope.” Proc. IDW, MEET1-3, (2014). [5] N. Miura, M. Kawanishi, H. Matsumoto, R. Nakano, “High-luminance blue-emitting BaAl2S4:Eu thin-film electroluminescence devices”, Japan. J. Appl. Phys., Part 2, 38, 1291 (1999). [6] Phosphor Handbook, 2nd ed., W. Yen, S. Shionoya and H. Yamamoto eds., CRC Press, Boca Raton (2007), Chapters 4 and 5.                 [7] M. Peng, G. Hong, “Reduction from Eu3+ to Eu2+ in BaAl2O4:Eu phosphor prepared in an oxidizing atmosphere and luminescent properties of BaAl2O4:Eu”, J.  Lumin. 127, 735 (2007). [8] J. H. Hao, J. Gao, “Abnormal reduction of Eu ions and luminescence in CaB2O4: Eu thin films”, Appl. Phys. Lett., 85, 3720 (2004). [9] R.J. Danby, Ultraviolet-induced charge transfer in CaSO4:Eu, J. Phys. C: Solid State Phys. 21, 485 (1988).   [10] A. Nag, T. R. N. Kutty, “The light induced valence change of europium in Sr2SiO4:Eu involving transient crystal structure”, J. Mater. Chem. 14, 1598 (2004). [11] E. Malchukova, B. Boizot, Reduction of Eu3+ to Eu2+ in aluminoborosilicate glasses under ionizing radiation, Mater. Res. Bull. 45, 1299 (2010).   [12] X. Gong, P. Wu, W.K. Chan, W. Chen, “Effect of J-ray irradiation on structures and luminescent properties of nanocrystalline MSO4:xEu3+ (M=Ca; Sr; Ba; x=0.001–0.005)”, J. Phys. Chem. Solids 61, 115 (2000). [13] A.R. Lakshmanan, A. Tomita, “Thermostimulated luminescence, exoelectron emission and X-Ray induced luminescence studies in CaSO4: Eu and CaSO4:Eu, Na”, phys. stat. sol. (a), 173, 503 (1999). [14] J. Qiu, K. Kojima, K. Miura, T. Mitsuyu, K. Hirao, “Infrared femtosecond laser pulse–induced permanent reduction of Eu3+ to Eu2+ in a fluorozirconate glass”, Optics Lett., 24, 786 (1999). [15] Alain Baumer, Philippe Blanc, Dominique Lapraz, Daniel Ohnenstetter, Fabien Cesbron, Gerard Panczer and Hildegarde Prevost, C.R. “Instability of Eu3+ ions under electron beam excitation observed by luminescence” Acad. Sci. Paris, Earth & Planetary Sciences, 329, 629-635, (1999).  535       IDW ’15

Blue and Red Cathodoluminescent Emission of Y2O3:Eu Phosphor Studied as a Function of Temperature in a Transmission Electron Microscope

http://bura.brunel.ac.uk/bitstream/2438/13917/1/PHp1-2.pdf

Blue and Red Cathodoluminescent Emission of Y2O3:Eu Phosphor Studied as a Function of Temperature in a Transmission Electron Microscope

Abstract