The micromagnetic structure in epitaxial (001)-oriented Cu/Ni(14 nm)/Cu rings fabricated by electron beam and focused ion beam lithographies with external diameter of 3 µm and linewidths between 100 and 500 nm is presented. We found that a state with radial orientation of the magnetization prevails at remanence. The evaluation of the magnetoelastic, magnetocrystalline and magnetostatic energies shows that a value as low as 1.5 × 10-3 for the anisotropic relaxation of the in-plane strain components is enough to induce an effective radial easy magnetization direction