 25th International Symposium on Analytical and Environmental Problems 117 PRELIMINARY STUDIES ON THE HYDROTHERMAL SYNTHESIS OF PROMISING MULTIFERROIC PIEZOCERAMICS FOR THE MEDICAL APPLICATIONS  Cristian Casut1,3, Raul Bucur1, Daniel Ursu1, Nicolae Miclau2, Paul Barvinschi3, Alina Zamfir1,3, Marinela Miclau1  1 National Institute for Research and Development in Electrochemistry and Condensed Matter, 1 Plautius Andronescu Street, 300224 Timisoara, Romania 2 Politehnica University Timisoara, Str. PiataVictoriei, nr.2, 300006 Timisoara, Romania 3 West University of Timisoara, Bulevardul Vasile Pârvan 4, Timișoara 300223 Timisoara, Romania  Abstract Lead-free piezoceramics aiming at replacing the market-dominant lead-based ones have been extensively searched for more than a decade worldwide [1]. From the beginning, the goal was obviously to develop lead-free piezoceramics whose properties are no less than those of the market-dominating lead zirconate titanate (PZT). With the functionality of interconverting mechanical and electrical energy, piezoelectric materials have the versatility to address a wide range of applications, including actuators, sensors, and transducer devices [2]. Multiferroics have been known to have ferromagnetic and ferroelectric properties at the same time, with interesting physical properties as well as the possibility of the practical applications for new memory devices. Multiferroic piezoceramics maintain considerable piezoelectricity, whilst presenting challenges in terms of processing of single-phase material. The synthesis of high-purity of BiFeO3 (BFO) ceramic using solid-state reaction is known to be very difficult due to inevitable formation of the secondary phases, mostly mullite-type Bi2Fe4O9 and sillenite-type Bi25FeO39 [3]. In this study, we report the synthesis and characterization of BiFeO3 by hydrothermal methods using Bi(NO3)3 5H2O and Fe(NO3)3 9H2O as precursors with a solution of 2M NaOH as mineralizer at a 200 ̊C temperature for 48 hours. In typical synthesis process, the precursors were mixed in 30 ml of water. a temperature of 200 ̊C, 48 hours. The structure of BiFeO3 was determined by powder X-ray diffraction (XRD) PW 3040/60 X’Pert PRO using Cu-Kα radiation with (λ=1.5418Å), in the range 2θ = 10-80°, at room temperature (Fig. 1a). A Scanning Electron Microscope InspectS (SEM) was used to observe the morphology of synthesized nanocrystals (Fig. 1b). The diffuse reflectance spectra (DSR) was obtained using a Lambda 950 UV-Vis-NIR Spectrophotometer with 150 mm integrating sphere in the wavelength range of 300–800 nm.          Figure 1. a)  X-ray diffraction patterns and b) SEM image of BiFeO3 obtained frrom hydrothermal methods using Bi(NO3)3 5H2O and Fe(NO3)3 9H2O as precursors with a solution of 2M NaOH as mineralizer at a 200 ̊C temperature for 48 hours.   25th International Symposium on Analytical and Environmental Problems 118 Acknowledgements  This project was supported by the Romanian National Authority for Scientific Research, UEFISCDI, through project PN-III-P1-1.2-PCCDI-2017-0046 and PN 19 22 04 01, no. 40N/2019.  References [1] Hong C-H, Kim H-P, Choi B-Y, Han H-S, Son JS, Ahn CW, Jo W, Lead-Free Piezoceramics - Where to Move on?, Journal of Materiomics (2016) [2] J. Koruza, A. J. Bell, T.Frömling, K. G. Webber, K. Wang, J. Rödel, Journal of Materiomics, 13-26 (2018). [3] H. Han, J. H. Lee, H. M. Jang, Inorganic Chemistry, 56 (19), 11911–11916 (2017).   

Preliminary studies on the hydrothermal synthesis of promising multiferroic piezoceramics for the medical applications

http://acta.bibl.u-szeged.hu/64795/1/proceedings_of_isaep_2019_117-118.pdf

Preliminary studies on the hydrothermal synthesis of promising multiferroic piezoceramics for the medical applications

Abstract