MIREA - Russian Technological University (RTU - MIREA).
Abstract
The time dependence of the mechanical losses of low density polyethylene (LDPE) filled with fine particles of shungite in the process of periodic dynamic loading at changing frequency of loading and temperature was studied. It was shown that upon increasing the filler concentration and loading frequency these dependences are either similar in nature or shifted in the time-temperature scale on the graphs. The temperature and time dependent parameters and the interpretation of their physical meaning were proposed. It was confirmed that development of relaxation processes occurs in filled polymers under dynamic loading. A relationship between the parameters of these processes is described by logarithmic and exponential functions. These dependencies are determined by both the polymer matrix and the transition polymeric layer formed on the filler surface.В работе проведено исследование зависимостей от времени механических потерь наполненного мелкодисперсными частицами шунгита полиэтилена низкой плотности (ПЭНП) в процессе периодического динамического нагружения при изменении частоты нагружения и температуры. Показано, что при увеличении концентрации наполнителя и частоты нагружения эти зависимости имеют либо идентичный характер, либо наблюдается сдвиг по шкале время–температура на соответствующих зависимостях. Предложены параметры, связывающие температурно-временные зависимости, и интерпретация их физического смысла. Подтверждено, что в наполненном полимере при динамическом нагружении происходит развитие релаксационных процессов, аппроксимируемых сложными логарифмическими и показательными функциями. Этот процесс определяется как самой полимерной матрицей, так и образующимся на поверхности наполнителя переходного полимерного слоя