CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Thickness-dependent in-plane thermal conductivity of suspended MoS2 grown by chemical vapor deposition
Authors
Byoung Hee Moon
Gang Hee Han
+7 more
Hye Yun Jeong
Hyun Kim
Jaesu Kim
Jung Jun Bae
Min Su Kim
Seong Chu Lim
Young Hee Lee
Publication date
1 October 2018
Publisher
ROYAL SOC CHEMISTRY
Abstract
The in-plane thermal conductivities of suspended monolayer, bilayer, and multilayer MoS2 films were measured in vacuum by using non-invasive Raman spectroscopy. The samples were prepared by chemical vapor deposition (CVD) and transferred onto preformed cavities on a Au-coated SiO2/Si substrate. The measured thermal conductivity (13.3 ± 1.4 W m−1 K−1) of the suspended monolayer MoS2 was below the previously reported value of 34.5 ± 4 W m−1 K−1. We demonstrate that this discrepancy arises from the experimental conditions that differ from vacuum conditions and small absorbance. The measured in-plane thermal conductivity of the suspended MoS2 films increased in proportion to the number of layers, reaching 43.4 ± 9.1 W m−1 K−1 for the multilayer MoS2, which explicitly follows the Fuchs-Sondheimer suppression function. The increase in the thermal conductivity with the number of MoS2 layers is explained by the reduced phonon boundary scattering. We also observe that the Fuchs-Sondheimer model works for the thickness-dependent thermal conductivity of MoS2 down to 10 nm in thickness at room temperature, yielding a phonon mean free path of 17 nm for bulk. © The Royal Society of Chemistry9
Similar works
Full text
Available Versions