Journal ArticleTransmission electron microscope (TEM) and transmission electron diffraction (TED) studies have been performed to investigate the effects of V/III ratio on ordering and antiphase boundaries (APBs) in organometallic vapor phase epitaxial Ga0.5In0.5P layers grown onto (001) GaAs vicinal substrates at 670 °C. TED and TEM examination showed that the degree of order is higher in the layer grown using a V/III ratio of 160 than in the layer grown using a V/III ratio of 40. TEM results showed that the higher V/III ratio could be used to suppress APBs. In addition, the growth of order-induced heterostructures, where the V/III ratio is increased abruptly during growth, could be used to block the propagation of APBs. Mechanisms are proposed to explain these phenomena