The ingots of CuTaAlSe3 and CuTaGaSe3 were synthesized using the melt and annealing technique. X-Ray Diffraction (XRD) and Differential Thermal Analysis (DTA) techniques were used for characterization of the alloy. The analysis of the diffraction pattern indicates that both samples are composed by two phases; the mean phase indexes as a hexagonal structure, whereas the secondary phase indexes as a tetragonal chalcopyrite-like structure. From the shape of the DTA peaks for the CuTaAlSe3 and CuTaGaSe3 alloys, was deduced that the melting is incongruent for both materials, value of ~1348K and ~1235K, respectively.
Los lingotes de CuTaAlSe3 y CuTaGaSe3 se sintetizaron usando la técnica de fusión y recocido. Se usaron técnicas de difracción de Rayos X (DRX) y Análisis Térmico Diferencial (ATD) para la caracterización de las aleaciones. El análisis del patrón de difracción, indica que ambas muestras están compuestas por dos fases; la fase promedio indexada como una estructura Hexagonal, mientras que la fase secundaria indexa como una estructura tetragonal de tipo calcopirita. De la forma de los picos del ATD para las aleaciones CuTaAlSe3 y CuTaGaSe3, se deduce que la fusión es incongruente para ambos materiales, de valor aproximado 1348K y 1235K, respectivamente