This study deals with the particularities of structure formation and hydration of the complex binder, which consists of liquid glass, metallurgical slag and high aluminate cement (Al2O3 > 70 %). According to the ultrasonic and exothermal temperature results, it was determined that due to the reaction between liquid glass and dicalcium silicate the highest hardening intensity was found in the first 20 minutes; however, the hydration of cement takes place much later, i.e. in the hardened structure. SEM investigations of the complex binder showed that its structure is dominated by areas where cement particles are joined by nanostructures (70%), struktūros formavimosi ir hidratacijos ypatumai kietėjimo metu. Ultragarso ir egzotermijos temperatūros tyrimais nustatyta, kad kompozicinis rišiklis dėl skystojo stiklo ir dikalcio silikato reakcijos sukietėja jau per pirmąsias 20 minučių, tačiau aliuminatinio cemento hidratacija vyksta daug vėliau, t.y. jau sukietėjusioje struktūroje. Tiriant kompozicinį rišiklį skenuojamuoju elektroniniu mikroskopu (SEM), nustatyta, kad struktūroje vyrauja plotai, kur cemento daleles sujungia skystojo stiklo ir kietiklio reakcijos produktų nanostruktūros (<50 nm), daugumos cemento dalelių paviršius padengtas 30 nm–100nm dydžio nanodalelių sluoksniais – cemento hidratacijos produktais