CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
激光熔覆conicraly高温合金格栅的高速刮削性能
Authors
兰昊
张伟刚
+4 more
张阳
李建保
骆丽杰
黄传兵
Publication date
1 January 2018
Publisher
Abstract
采用光纤激光同轴送粉技术制备了CoNiCrAlY高温合金格栅结构熔覆层,采用模拟飞机发动机叶尖高速刮削试验机研究了熔覆层的刮削性能。采用扫描电子显微镜、三维数字显微镜、激光共聚焦显微镜、显微硬度计等对合金格栅的微观结构和力学性能进行了分析测试。结果表明:研制的熔覆层具有致密的微观组织,物相组成与前驱粉末基本一致;熔覆层的维氏显微硬度值为(357±20)HV0.2;1 000℃热处理后的熔覆层与处理前的组织结构无太大区别,维氏显微硬度值为(345±20)HV0.2;在相同刮削实验参数条件下,间距2、3和4 mm格栅结构的磨损量差别较大,其中3 mm格栅结构及其对摩的叶片的质量损失都最小,且摩擦振动较小,表明间距为3 mm格栅结构的可刮削性能优于间距为2 mm和4 mm格栅结构
Similar works
Full text
Available Versions
Institutional Repository of Institute of Process Engineering, CAS (IPE-IR)
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:ir.ipe.ac.cn:122111/34536
Last time updated on 05/12/2019