                       General rights Copyright and moral rights for the publications made accessible in the public portal are retained by the authors and/or other copyright owners and it is a condition of accessing publications that users recognise and abide by the legal requirements associated with these rights.  • Users may download and print one copy of any publication from the public portal for the purpose of private study or research. • You may not further distribute the material or use it for any profit-making activity or commercial gain • You may freely distribute the URL identifying the publication in the public portal   If you believe that this document breaches copyright please contact us providing details, and we will remove access to the work immediately and investigate your claim.     Downloaded from orbit.dtu.dk on: Dec 20, 2017Structure and strength in graded nanostructured steelZhang, Xiaodan; Hansen, Niels; Gao, Yukui ; Huang, XiaoxuPublished in:Abstract BookPublication date:2013Link back to DTU OrbitCitation (APA):Zhang, X., Hansen, N., Gao, Y., & Huang, X. (2013). Structure and strength in graded nanostructured steel. InAbstract Book (pp. 222)Structure and strength in graded nanostructured steel  Xiaodan Zhang1, Niels Hansen1, Yukui Gao2, Xiaoxu Huang1 1. Danish-Chinese Center for Nanometals, Section for Materials Science and Advanced Characterization, Department of Wind Energy, Risø Campus, Technical University of Denmark, DK-4000 Roskilde, Denmark 2. School of Aerospace Engineering and Applied Mechanics, Tongji University, Shanghai 200092, China  The  structure  and  strength  of  low  carbon  steel  samples  have  been  analyzed  after  plastic deformation by shot‐peening and cold‐rolling. The  fine scale surface microstructure caused by shot‐peening extends to ∼50 μm below the surface. The structure is graded and subdivided by dislocation boundaries and high angle boundaries showing a clear resemblance to the  lamellar structure, which evolves during conventional rolling of bulk metallic materials from medium to high  strain. As  the  surface  is  approached,  the boundary  spacing decreases  to ∼50 nm  at  the surface. In parallel, the misorientation angle across boundaries increases to ∼65% of high angle boundaries. The  cold‐rolled  steel  shows a  low hardening  rate at high  strain and by assuming additive strength contributions  from Hall–Petch and dislocation strengthening,  the  flow stress has been  expressed by  the  relationship  , where Dav  is  the  average  spacing between  the  low  and  high  angle  boundaries  which  subdivide  the  microstructure,  σ0  is  the friction stress and k2  is a number which  is expressed  in  terms of structural parameters which have been determined by electron backscattered diffraction. It is found that calculated k2 values are  in  accord  with  an  experimental  value  of  310 MPa μm0.5.  In  the  shot‐peened  steel  the increase  in Dav with  increasing  distance  from  the  surface  is  transformed  into  a  stress profile based on the σ ‐ Dav relationship established for cold‐rolled bulk samples. The calculated stress profile  is  validated  by  comparison  with  the  experimental  profile  based  on  hardness measurements, and good agreement  is  found. This  result points  to a wider application of  the suggested method  to  derive  the  local  flow  stress  in  a  deformed microstructure  based  on  a measurement of  the  local boundary spacing and the stress–structure  relationship  for the bulk material in the deformed state.  Reference:  [1] Hall–Petch and dislocation strengthening in graded nanostructured steel. Xiaodan Zhang, Niels Hansen, Yukui Gao, Xiaoxu Huang. Acta Materialia 2012; 60: 5933 5943.‐   

Structure and strength in graded nanostructured steel

http://orbit.dtu.dk/ws/files/72266355/Structure_and_strength_in_graded_nanostructured_steel.pdf

Structure and strength in graded nanostructured steel

Abstract

Similar works

Full text

Available Versions

Online Research Database In Technology