Square-form, multi-layered nanofilter membranes have been investigated experimentally and by numerical simulation to determine their load bearing capacity versus filtration ability. The effect of various topologies combining the thickness of a load-carrying layer and Si-reinforcement on the bursting pressure has been determined. Based upon the comparison of a performance index an optimal structure could be selected for later production

Kovacs, Andras

Kovács, Ádám

English

Periodica Polytechnica (Budapest University of Technology and Economics)

83Increase of load bearing capacity of a square-form nanofilter 2014 58 2Increase of load bearing  capacity of a square-form nanofilterÁdám Kovács, Andras Kovacsreceived 19 OctOber 2013; accepted after revisiOn 9 april 2014AbstractSquare-form, multi-layered nanofilter membranes have been investigated experimentally and by numerical simulation to determine their load bearing capacity versus filtration abil-ity. The effect of various topologies combining the thickness of a load-carrying layer and Si-reinforcement on the bursting pressure has been determined. Based upon the comparison of a performance index an optimal structure could be selected for later production.Keywordsnanofiltration · multi-layered membrane · porous structure1 IntroductionPorous silicon is found in many applications, e.g. sensors, tissue engineering, medical therapeutics and diagnostics, pho-tovoltage, rechargeable batteries, energetic materials, photon-ics and also in micro-electromechanical systems (MEMS) [1]. Depending on the pore sizes its structure can serve for filtration purposes from nano- to microfiltration. The filtration capacity depends mostly on the porosity, which – unfortunately – dimin-ishes the strength, and consequently, the load bearing capacity of the system. Several reinforcement solutions are known to in-crease the bursting (critical) pressure of the structure, e.g. built-in extra layer having high strength (e.g. silicon-nitride, SiN), single-crystal silicon (cSi) columns, or the combination of them.The investigated membranes are square-formed, made from a very thin perforated silicon-nitride (SiN) layer on a much thicker porous silicon (PS) layer, which is supported and rein-forced by single-crystal silicon (c-Si) columns (Fig. 1).The figure is not scaled, it only shows the structure of the filter membrane. Since this base structure is fabricated by a wet etching technology from a thick wafer, a very stiff thick silicon frame remains around the membrane.Three main types of configuration have been fabricated, as-signed by A, B and C (Fig. 2). In order to obtain higher fil-tration rate the porosity should be as high as possible which diminishes the strength, and consequently, the load capacity of the device. This effect can be compensated by application of thicker SiN support layer and/or cSi-columns as a support grid within the PS-layer.58(2), pp. 83-86, 2014DOI:10.3311/PPme.7124Creative Commons Attribution bresearch articleÁdám KovácsDepartment of Applied Mechanics, Faculty of Mechanical Engineering,Budapest University of Technology and Economics,Műegyetem rkp. 3., H-1111 Budapest, Hungarye-mail: adamo@mm.bme.huAndras KovacsFaculty of Computer and Electrical Engineering, Furtwangen University,Robert-Gerwig-Platz 1, 78120 Furtwangen, Germanye-mail: kovacs@hs-furtwangen.deFig. 1. Sketch of porous nanofilterP Periodica Polytechnica Mechanical Engineering84 Period. Polytech. Mech. Eng. Ádám Kovács, Andras KovacsAll three types have an upper thin SiN-layer, and a thick PS-layer. Changes are made by depositing extra cSi-reinforcement of different amount (Types A and B), as well as by changing the porosity and the thickness of the layers within one type.Silicon and silicon-nitride are commonly considered as brit-tle elastic materials, therefore their two fundamental material parameters corresponding to strength and load bearing capacity are the elastic modulus and the fracture strength. The higher the porosity is, the less is the elastic modulus of the structure. On the other hand, the load bearing capacity can directly be characterized by the bursting pressure, which determines the fracture strength of the material. For high filtration large poros-ity is required; however, a good load bearing capacity is also desirable. Since porosity and large fracture strength contradict each other, one should find an optimal configuration. This op-timum can be searched for by creating a performance index f, which is simply defined as a rate of the fracture strength (σ B) and the elastic modulus (E). Largest value of this index shows the optimum.2 Experimental workThe experimental set-up (Fig. 3) consists of a pressure box, where the test structure was put, a microscope and a camera.The maximum deflection of the samples made from the base materials (cSi, SiN) has been detected by a computer connected to the camera, while the bursting pressure was registered by another computer connected to the manometer between the air-pressure control unit and the pressure box (Fig. 4).Elastic moduli of the base materials have been determined analytically from the measured middle-point deflection using the elastic thin plate theory [2]. The effective elastic modulus needed for the performance index of the whole membrane was then calculated by a simple averaging method [3] from the elas-tic moduli of the upper layer and the cSi-reinforcement. The elastic modulus of the porous silicon layer was detemined by the simple formulaE P Ep = −( )1suggested by van Rijn [4], where P is the porosity rate.Fracture strength was calculated by using the maximum nor-mal stress theory commonly applied for brittle materials:where σ1  is the maximum principal stress in the plate. Simi-larly to the calculation of E, an analytical estimate has been made for the relationship between the measured bursting pres-sure pcrit and [2].Fig. 3. Measurement set-up Fig. 4. Scheme of the experimental set-upFig. 2. Test structure configurationsσ σf = 1 maxσ185Increase of load bearing capacity of a square-form nanofilter 2014 58 23 Results and discussionA series of seven different structures have been produced from the three major types (Table 1).One specimen was produced from Type A structure, 3-3 pieces from Types B and C. They differed in the side-length of the square plate (L), and the thicknesses of the upper SiN (h_SiN) and the porous silicon layer (h_PS), respectively. The thickness values are rounded to thousandts.Figure 5 shows the variation of the calculated elasticity modu-lus versus the the applied pressure in the case of the B1 structure.It is clearly seen in Fig. 5 that a minimum pressure should be applied to obtain a stable material parameter. This can be explained by the uncertain measurement at very low pressure. Zooming-in to the right-hand part of the diagram the value of E becomes almost constant (Fig. 6), which proves this statement.Similar feature have been experienced in the case of all other structures.Figure 7 shows the maximum deflection of the membrane as a function of the applied pressure for three typical structures (A, B2 and C3).The last points in the graphs represent the bursting pres-sures of the chips. The diagram shows a slightly nonlinearity between wmax and p, which is due to perforation of the upper layer. This nonlinearity has been already reported in [5].Table 2 summarizes the numerical results for the calculated material parameters, as well as the performance indeces.These results show that although structures of Type C do not contain added cSi-reinforcement, and consequently, their frac-ture strengths are much less, than those of the other two chip types, the resulting softness is compensated by much higher filtration ability. The applicability of this structure type highly depends on the working pressure of the filtered medium. If the  0204060801001200,02 0,06 0,10 0,14 0,18 0,22p (Pa)E_exp (GPa)   0100020003000400050000 0,005 0,01 0,015 0,02 0,025p  [MPa]E [GPa]K1 K20102030405060700 100 200 300 400 500 600 700 800 900p  [mbar]w_max [µm]Chip AChip B2Chip C3 0204060801001200,02 0,06 0,10 0,14 0,18 0,22p (Pa)E_exp (GPa)   0100020003000400050000 0,005 0,01 0,015 0,02 0,025p  [MPa]E [GPa]K1 K20102030405060700 100 200 300 400 500 600 700 800 900p  [mbar]w_max [µm]Chip AChip B2Chip C3 0204060801001200,02 0,06 0,10 0,14 0,18 0,22p (Pa)E_exp (GPa)   0100020003000400050000 0,005 0,01 0,015 0,02 0,025p  [MPa]E [GPa]K1 K20102030405060700 100 200 300 400 500 600 700 800 900p  [mbar]w_max [µm]Chip AChip B2Chip C3Fig. 5. Change of estimated elasticity modulus vs. applied pressure (B1 structure) – total pressure rangeFig. 6. Change of estimated elasticity modulus vs. applied pressure (B1 structure) – high pressure rangeFig. 7. Variation of the maximum deflection of the membrane vs. applied pressureTab. 1. Geometrical parameters of test structures A B1 B2 B3L (μm) 1500 1000 1500 1500h_SiN (μm) 0,085 0,050 0,050 0,050h_PS (μm) 23 25 27 20C1 C2 C3L (μm) 1500 1000 1000h_SiN (μm) 0,052 0,051 0,052h_PS (μm) 21 20 29Tab. 2. Calculated material parameters and performance indeces A B1 B2 B3E [GPa] 14.63 10.69 10.83 11.87σ B  [MPa] 303.9 280.1 278.0 287.20.0208 0.0262 0.0257 0.0242C1 C2 C3E [GPa] 5.94 5.94 5.87 [MPa] 251.4 251.5 251.00.0423 0.0423 0.0428f EB= σ /f EB= σ /σ B86 Period. Polytech. Mech. Eng. Ádám Kovács, Andras Kovacspressure could be kept under 700 mbar (see Fig. 7), Type C would be chosen as optimum. For this type of structures the performance index is almost constant, which demonstrates the importance of the upper SiN-layer. The side length of the mem-brane and the thickness of the porous layer played much less role in the results.4 ConclusionsThe key issue in assessment of applicabilty of multi-layered micro or nanofilters is the determination of their elasticity modulus and fracture strength. Once we know them, the perfor-mance index helps us to choose the optimal design. In order to get stable E-values, the test pressure must exceed the minimum pressure. In our experiments this was about 60 mPa.The ultimate strength can be determined from the bursting (critical) pressure, which is the principal quantity of load bear-ing capacity.The presence of single crystal reinforcement columns leads to a clear decrease of maximum deflection (~ 1/E) and maxi-mum normal stress (~ 1/pcrit). The fracture strength is mainly affected by the thickness of the upper silicon-nitride layer and is hardly modified by the thickness of the porous silicon layer. Among the pre-concepts of design, the structure of Type C showed the best performance index.References1 Sailor M. J., Porous Silicon in Practice. Wiley-VCH Verlag (2011).2 Kovács Á., Kovács A., Mescheder U., Estimation of elasticity modulus and fracture strength of thin perforated SiN membranes with finite element simulations. Computational Materials Science, 43 (1), pp. 59-64, (2008). DOI: 10.1016/j.commatsci.2007.07.0233 Kovács Á., Kovacs A., Effect of silicon reinforcement on load-capacity of porous nanofilters. Proceedings in Applied Mathematics and Mechanics, 8 (1), pp. 10215-10216, (2008). DOI: 10.1002/pamm.2008102154 van Rijn C. J. M., Nano and Micro Engineered Membrane Technology. Elsevier, Amsterdam (2004).5 Kovács A., Kovacs Á., Pogány M., Mescheder U., Mechanical investigation of perforated and porous membranes for micro- and nanofilter applications. Sensors and Actuators B: Chemical, 127 (1), pp. 120-125, (2007). DOI: 10.1016/j.snb.2007.07.044

Increase of load bearing capacity of a square-form nanofilter

https://pp.bme.hu/me/article/download/7124/6727

Increase of load bearing capacity of a square-form nanofilter

Abstract

Similar works

Full text

Available Versions

Periodica Polytechnica (Budapest University of Technology and Economics)