Two kinds of optical fibers were irradiated in a fission reactor, JMTR(Japan Materials Testing Reactor), up to a 1.55x10^n/cm^2 fast neutron fluence and a 3.3x10^9Gy ionizing dose at 370K. Optical transmission spectra were measured in the wavelength range of 450-1750nm, in-situ. Growth of strong optical absorption bands were observed in the range of wavelength shorter than 750nm. In the meantime, the fibers showed good radiation-resistance in the range of wavelength longer than 750nm. Optical radiations were observed from SiO_2 optical fibers under irradiation. A major part of the observed optical radiations is thought to be composed of broad optical radiation in the whole wavelength range studied in the present experiment. This broad optical radiation will be generated by the process of so-called Cerenkov radiation. Also, a sharp optical radiation peak was found at 1270nm on a F-doped fiber. This peak is thought to relate with doped Fluorine ions and ionizing gamma-ray irradiation