'National University of Science and Technology MISiS'
Doi
Abstract
The study covers the impact of thermo-time processing and cooling rate of molten metal on the crystallization regularities, structure, properties and modifying ability of Al–Sc alloys. The Al–Sc alloys obtained by electrolysis in the KF–NaF–AlF3–Sc2O3 melts at 820–850 °C were used as an initial charge for casting. It was found that changes in overheat values and casting temperatures make it possible to vary the shape, number and size of crystals in a wide range. The modifying effect of the cast and fast-quenched master alloys and alloy produced by electrolysis was tested on Al–4,5%Cu alloys. The greatest refinement of the Al–4,5%Cu–0,4%Sc alloy structure was obtained with the fast-quenched master alloy.Исследовано влияние режимов термовременной обработки и скорости охлаждения металлических расплавов на закономерности кристаллизации Al–Sc-сплавов, их структуру, свойства и модифицирующую способность. В качестве исходной шихты для литья использовали отливки Al–Sc-сплавов, полученные электролизом солевых расплавов KF–NaF– AlF3–Sc2O3 при 820–850 °С. Установлено, что, меняя величину перегрева расплава и температуру литья, можно в широких пределах варьировать форму, количество и размеры кристаллов. Модифицирующее действие литой и быстрозакаленной лигатур, а также лигатурного сплава, полученного электролизом, протестировано на сплавах Al–4,5%Cu. Наибольший эффект измельчения структуры сплава Al–4,5%Cu–0,4%Sc был достигнут при использовании быстрозакаленной лигатуры