The International Institute for Science, Technology and Education (IISTE)
Abstract
A Ni–B coating was electroless-deposited directly on H3PO4/HF pickled AZ31. The thickness of the plating layer was estimated through weight gain measurements and was affected by temperature, time and bath composition. The highest thickness was obtained at 6 g/L of NaHB4 at 85oC. An adherent compact layer of Ni-B was obtained. Electrochemical impedance spectroscopy measurements in 3.5 wt.% sodium chloride aqueous solution suggest that the plating can protect the magnesium alloy substrate from corrosion attack