Bamboo (Bambusa vulgaris) waste were used as a raw material for producing activated carbon (AC). The materials were collected and turned into AC by carbonization (500 °C, 1.67 °C.min-1, 60 min) and activation (800 °C, 10 °C.min-1, 60 min) processes with CO2 (100 mL.min-1). The obtained material (CO2 AC) was characterized by its yield, elemental analysis, ash content, methylene blue and iodine indexes, surface area (SBET), Boehm titration method, scanning electron microscopy and used as adsorbent for removing the methylene blue and phenol contaminants. The Langmuir and Freundlich isotherms models were selected for understanding the adsorption process. CO2 AC produced showed yield of 21.6%, carbon content of 82.13% and SBET of 856.78 m2.g-1, presenting rapid removal and high adsorption capacity for methylene blue (298.82 mg.g-1) and phenol (558.29 mg.g-1).Resíduos de bambu (Bambusa vulgaris) foram utilizados como matéria-prima para a produção de carvão ativado (CA). Os materiais foram coletados e transformados em CA mediante processos de carbonização (500ºC, 1,67 ºC min-1, 60 min) e ativação (800 ºC, 10 ºC min-1, 60 min) com CO2 (100 mL min-1). O material obtido (CA CO2) foi caracterizado pelo seu rendimento, análise elementar, teor de cinzas, índices de azul de metileno e de iodo, área superficial (SBET), método titulométrico de Boehm, microscopia eletrônica de varredura e utilizado como adsorvente para remoção dos contaminantes azul de metileno e fenol. Os modelos de isotermas de Langmuir e de Freundlich foram selecionados para entender o processo de adsorção. O CA CO2 produzido apresentou rendimento de 21,6%, teor de carbono de 82,13% e SBET de 856,78 m2 g-1, apresentando uma remoção rápida e elevada capacidade de adsorção para o azul de metileno (298,82 mg g-1) e fenol (558,29 mg g-1)