In this study Dynamic Mechanical Anlaysis (DMA) was applied to dentin, the macro hybrid layer and intact hybrid layers of the bonded dental restorative interface using nanoindentation. Both intertubular and peritubular dentin were evaluated by DMA using discrete and scanning mode nanoindentation. The complex (E*), loss (E), and storage (E') moduli were quantified over a range of indentation loads and scanning frequencies. The storage modulus of the peritubular cuff (22.19 GPa0.05). A model bonded interface (i.e. the macro hybrid) was evaluated using scanning DMA. A new approach for hydrating samples using ethylene glycol solution was developed and then applied to identify the importance of hydration on the measured properties. Fully hydrated samples exhibited mean values of E*, E' and E of 3.54 GPa, 3.42 GPa and 0.86 GPa, respectively, whereas fully dehydrated samples exhibited values of 4.01 GPa, 3.88 GPa and 0.94 GPa, respectively. There were significant differences in the complex modulus (p0.05). A dynamic loading frequency of 100 Hz and scanning frequency of 0.2 Hz were identified to provide the most reliable results in scanning the collagen-based systems. Lastly, the optimal testing parameters obtained from studying the macro hybrid layer were used to evaluate intact resin-dentin bonded interfaces. The property maps clearly distinguished variations in properties as a function of the constituents. It was identified that scanning based nanoDMA is a potent tool for evaluating mechanical properties of the hybrid layer but testing parameters and maintenance of the hydration are critical to the interpretation of apparent mechanical behavior