CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Impact of Modifier Oxides on Mechanical and Radiation Shielding Properties of B2O3-SrO-TeO2-RO Glasses (Where RO = TiO2, ZnO, BaO, and PbO)
Authors
B. H. Elesawy
M. Kh. Hamad
+6 more
M. U. Khandaker
K. A. Mahmoud
M. H. A. Mhareb
K. A. Naseer
H. Osman
M. I. Sayyed
Publication date
1 January 2021
Publisher
'MDPI AG'
Abstract
The influence of modifier oxides (TiO2, ZnO, BaO, and PbO) on the mechanical and radiation shielding properties of boro-tellurate glasses is investigated. Samples with a composition of B2O3-SrO-TeO2-RO (RO represents the modifier oxides) were fabricated using the melt quench method, and their physical, mechanical, and radiation attenuation parameters were reported. For this aim, Monte Carlo simulation was employed to predict the radiation attenuation parameters, while the Makishima-Mackenzie model was adopted to determine the mechanical properties. The tightly packed structure with better cross-linkage density is possessed by the Ti-containing glass (SBT-Ti) system among the titled glass batch. The higher Poisson and micro-hardness values of the SBT-Ti glass indicate its structure’s reduced free volume and better compactness. For the glass with PbO, the linear and mass attenuation coefficients are highly increased compared to those glasses doped with TiO2, ZnO, and BaO. The thinner half-value layer was reported at 0.015 MeV, taking values 0.006, 0.005, 0.004, and 0.002 for samples with TiO2, ZnO, BaO, and PbO, respectively. SBT-Pb sample (with PbO) has a thinner HVL compared to other fabricated glass samples. The fabricated glasses’ thickness (Deq) equivalent to 1 cm of lead (Pb) was reported. The results demonstrated that Deq is high at low energy and equals 11.62, 8.81, 7.61, 4.56 cm for SBT-Ti, SBT-Zn, SBT-Ba, and SBT-Pb glass samples, respectively. According to the Deq results, the fabricated glasses have a shielding capacity between 30 and 43% compared to the pure Pb at gamma-ray energy of 1.5 MeV. At high energy (8 MeV), the transmission factor values for a thickness of 1 cm of the fabricated samples reach 88.68, 87.83, 85.95, and 83.11% for glasses SBT-Ti, SBT-Zn, SBT-Ba, and SBT-Pb, respectively. © 2021 by the authors. Licensee MDPI, Basel, Switzerland.The authors acknowledge the support of Taif University Researchers Supporting Project number (TURSP-2020/127), Taif University, Taif, Saudi Arabia
Similar works
Full text
Available Versions
Institutional repository of Ural Federal University named after the first President of Russia B.N.Yeltsin
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:elar.urfu.ru:10995/111684
Last time updated on 17/05/2022