CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Characterization of Excessive Sm3+containing Barium Titanate Prepared by Tartrate Precursor Method
Authors
A. M. Dorgham
M. A. Hamad
O. M. Hemeda
A. M. A. Henaish
Publication date
1 January 2020
Publisher
'Elsevier BV'
Abstract
The [Formula presented](BST) samples, where (x = zero, 0.05, 0.1, 0.15, 0.2 and 0.3), have been successfully synthesized by tartrate precursor method at annealing temperature of 600°C under atmospheric pressure. The results revealed that the Sm content causes a decrease in both tetragonality and average grain size of BST samples. The electrical resistivity of BST samples is improved by low Sm content, reaching maximum value at x = 0.15 and then decreases with higher Sm content, suggesting that the conduction has two types of polaron hoping and semiconductor band conduction mechanisms at low and at high temperature ranges, respectively. It is demonstrated that the majority of charge carriers are p-type. The dielectric properties varies nonmonotonically with samarium content, showing strongly enhancement in dielectric constant for high Sm doping samples. It is recommended that BST samples are attractive for capacitor and energy storage applications. © 2020 The Author(s).This project was supported financially by the Academy of Scientific Research and Technology (ASRT) Egypt, Grant No. 6550 . ASRT is the 2nd affiliation of this research
Similar works
Full text
Available Versions
Institutional repository of Ural Federal University named after the first President of Russia B.N.Yeltsin
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:elar.urfu.ru:10995/111981
Last time updated on 17/05/2022