CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
On the electropolishing and anodic oxidation of Ti-15Mo alloy
Authors
D. Babilas
M. Basiaga
+11 more
S. O. Cholakh
D. M. Korotin
M. Krok-Borkowicz
E. Z. Kurmaev
A. Maciej
E. Pamuła
W. Simka
M. Sowa
L. Szyk-Warszyńska
E. Urbańczyk
I. S. Zhidkov
Publication date
1 January 2016
Publisher
'Elsevier BV'
Doi
Cite
Abstract
This paper presents research on modifying the surface of Ti-15Mo alloy using electropolishing and anodic passivation. The electropolishing process was carried out in solutions containing sulfuric acid, ethylene glycol, ammonium fluoride and oxalic acid. Whereas a voltage range from 20 to 100 V and a 1 M orthophosphoric acid solution were used during the anodic passivation. The influence of above mentioned processes parameters on the quality of the obtained oxide layer on Ti-15Mo alloy was investigated. The analysis of Ti-15Mo surface after modification was performed using scanning electron microscopy (SEM), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectroscopy (XPS), ellipsometry, and mechanical tests. Moreover, the corrosion resistance was investigated using a potentiostatic method in Ringer's solution. It was found that electropolishing leads to an increase in the surface homogeneity and to the form of an oxide layer, which consisted of TiO2 and MoO3. Whereas the oxide layers obtained during anodic passivation were characterized by different properties depending on the applied voltage. The anodic passivation at various voltages (20-100 V) increased the surface wettability (94.5°-87.6°) in comparison to the electropolished sample (97.5°). Moreover, the obtained oxide layer after anodization exhibited a high hardness. The electrolytic polishing and anodic passivation of Ti-15Mo also improved corrosion resistance of the alloy in contact with Ringer's solution. The sample anodized at 80 V presented the highest corrosion resistance by the smallest corrosion current density (1.4 nA cm-2) and the highest polarization resistance (37.4 MΩ cm2). © 2016 Elsevier Ltd. All rights reserved
Similar works
Full text
Available Versions
Institutional repository of Ural Federal University named after the first President of Russia B.N.Yeltsin
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:elar.urfu.ru:10995/102248
Last time updated on 06/11/2021